| 001 Hak Akses (open/membership) | open |
| 700 Entri Tambahan Nama Orang | Anne Zulfia, promotor; Eddy Sumarno Siradj, co-promotor; Bambang Sugiarto, examiner; Johny Wahyuadi Mudaryoto, examiner; Dedi Priadi, examiner; Sutopo, examiner; Rudi Subagja, examiner; Derry Pantjadarma, examiner |
| 336 Content Type | text (rdacontent) |
| 264b Nama Penerbit | Universitas Indonesia |
| 710 Entri Tambahan Badan Korporasi | Universitas Indonesia. Fakultas Teknik |
| 049 No. Barkod | 07-17-021033839 |
| 504 Catatan Bibliografi | |
| 852 Lokasi | Perpustakaan UI, Lantai 3 |
| 338 Carrier Type | volume (rdacarrier); online resource (rdacarrier) |
| 590 Cat. Sumber Pengadaan Koleksi | Deposit |
| 903 Stock Opname | RDA-Wiradha2017 |
| 053 No. Induk | 07-17-021033839 |
| Tahun Buka Akses | |
| 653 Kata Kunci | komposit matriks keramik; dimox; vickers |
| 040 Sumber Pengatalogan | LibUI ind rda |
| 245 Judul Utama | Komposit matriks keramik AL2O3/AI hasil proses directed melt oxidation (Dimox) |
| 264c Tahun Terbit | 2012 |
| 650 Subyek Topik | Directed melt oxidation |
| 850 Lembaga Pemilik | Universitas Indonesia |
| 520 Ringkasan/Abstrak/Intisari | Komposit keramik yang berbasis Al2O3 adalah material yang potensial untuk aplikasi temperatur tinggi. Reaksi antarmuka yang terjadi diantara matriks dan penguat penting dan merupakan penentu atau peran kunci dalam kemajuan aplikasi dari komposit keramik. Proses directed metal oxidation (dimox) merupakan salah satu proses pembuatan komposit matriks keramik yang fleksibel dan menawarkan kemampuan untuk membentuk komposit near-net shape dengan bermacam-macam komposisi dan mikrostruktur. Keberhasilan pembuatan komposit Al2O3/Al dengan proses ini dipengaruhi oleh dopant, waktu tahan, temperatur dan atmosfir tempat berlangsungnya proses.
Penelitian ini dilakukan dalam rangka menghasilkan komposit matriks keramik yang memiliki sifat mekanik yang baik dan antarmuka yang baik pula sebagai hasil dari reaksi antarmuka matriks dan penguat dalam meningkatkan ketangguhan dari matriks keramik. Temperatur proses yang digunakan 1100°C, 1200°C dan 1300°C dengan lamanya pemanasan 10 jam, 15 jam dan 24 jam untuk lingkungan atm dan temperatur proses yang digunakan untuk lingkungan N2 adalah 1100°C, 1150°C dan 1200°C dengan lamanya pemanasan 15 jam dengan persentase Mg sebagai dopant 5, 8, 10, 12 %. Hasil penelitian menunjukkan kedalaman infiltrasi maksimum dicapai pada waktu tahan proses 24 jam dengan 12% Mg dan temperatur 1300°C sebesar 29,34 mm, densitas maksimum dicapai pada waktu tahan proses 24 jam dengan 8% Mg pada temperatur 1100°C sebesar 3,50 gr/cm3, kekerasan mikro optimum dicapai pada waktu tahan proses 24 jam dengan 8% Mg dan temperatur 1100°C sebesar 1221 VHN, nilai fracture toughness maksimum pada waktu tahan proses 24 Jam dengan persentase 5% Mg dan temperatur 1300°C sebesar 8,25 MPa.m1/2. Reaksi antarmuka yang terbentuk dalam KMK Al2O3/Al adalah Al2O3, MgAl2O4, Mg3N2, AlN, AlSiO and MgSiO3.
Al2O3 based ceramic composites are potential materials for advanced temperature applications. Interfacial reaction that °Ccurs between the matrix and the reinforcement is the critical, determinant and the key role in advancing the application of ceramic composites. Directed melt oxidation (dimox) pr°Cess is one of the flexible way to produce ceramic matrix composites that offer the ability to form near-net shape composites in various compositions and microstructures. The successful manufacturing of Al2O3/Al composite using dimox pr°Cess is influenced by the dopant, holding time, temperature and the atmospheric circumstances on the site of the pr°Cess. The research was performed in order to produce ceramic matrix composites that have reliable mechanical properties and good interface as a result of matrix interface and reinforcement reaction in improving the toughness of matrix ceramic. Pr°Cess temperature was set up at 1100 °C, 1200 °C and 1300 °C for 10 hours, 15 hours and 24 hours in furnace atmosphere, while the temperature pr°Cess was set up at 1100 °C, 1150 °C and 1200 °C in N2 atmosphere for 15 hours with the same Mg content various from 5, 8, 10 and 12% wt of Mg as the dopant. The results indicated that the maximum depth of infiltration was 29.34 mm achieved in 24 hours sample with 12% wt of Mg at 1300 °C. Generated density was 3.50 gr/cm3 which was the maximum density after 24 hours of the pr°Cess with 8% wt of Mg at 1100 °C. The optimum microhardness of 1221 VHN was achieved in 24 hours at 1100 °C with 8% wt of Mg. The maximum value of fracture toughness of 8.25 MPa.m1/2 which was achieved in 24 hours for sample with 5% wt of Mg at 1300 °C. The interfacial reaction was analyzed by XRD, content of phase that was formed by Al2O3/Al CMCs were Al2O3, MgAl2O4, Mg3N2, AlN, AlSiO and MgSiO3. |
| 904b Pemeriksa Lembar Kerja | Laely |
| 090 No. Panggil Setempat | D1282 |
| d-Entri Utama Nama Orang | |
| 500 Catatan Umum | |
| d-Entri Tambahan Nama Orang | |
| 337 Media Type | unmediated (rdamedia); computer (rdamedia) |
| 526 Catatan Informasi Program Studi | Teknik Metalurgi dan Material |
| 100 Entri Utama Nama Orang | G.N. Anastasia Sahari, author |
| 264a Kota Terbit | Depok |
| 300 Deskripsi Fisik | xvii, 179 pages : illustration ; 29 cm + appendeix |
| 904a Pengisi Lembar Kerja | Sutiman, Nisrina Fairus Widiasmara |
| Akses Naskah Ringkas | |
| 856 Akses dan Lokasi Elektronik | |
| 502 Catatan Jenis Karya | Disertasi |
| 041 Kode Bahasa | ind |