| 001 Hak Akses (open/membership) | membership |
| 700 Entri Tambahan Nama Orang | Azwar Manaf, supervisor |
| 336 Content Type | text (rdacontent) |
| 264b Nama Penerbit | Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia |
| 710 Entri Tambahan Badan Korporasi | Universitas Indonesia. Fakultas Matematika dan Ilmu Pengetahuan Alam |
| 049 No. Barkod | 11-22-38334937 |
| 504 Catatan Bibliografi | pages 6-7 |
| 852 Lokasi | Perpustakaan UI |
| 338 Carrier Type | volume (rdacarrier); online resource (rdacarrier) |
| 590 Cat. Sumber Pengadaan Koleksi | |
| 053 No. Induk | 11-22-38334937 |
| Tahun Buka Akses | |
| 653 Kata Kunci | magnesium alloy; casting; solution treatment; microstructure; hardness |
| 040 Sumber Pengatalogan | LibUI eng rda |
| 111 Entri Utama Nama Pertemuan | |
| 245 Judul Utama | Enhancing the hardness of Mg-9Al-1Zn cast alloy by Solution Treatment = Meningkatkan kekerasan paduan Cor Mg-9Al-1Zn melalui Solution Treatment |
| 650 Subyek Topik | Enhancing the hardness |
| 264c Tahun Terbit | 2019 |
| 850 Lembaga Pemilik | Universitas Indonesia |
| 904b Pemeriksa Lembar Kerja | Nurbaini |
| 520 Ringkasan/Abstrak/Intisari | Paduan magnesium merupakan bahan ringan yang memiliki potensi besar untuk dikembangkan karena paduan tersebut dapat mengurangi konsumsi energi dan berat total. Paduan ini terbuat dari logam magnesium sebagai komponen utama yang dicirikan oleh kekuatan rendah yang lembut dan mekanis. Penambahan aluminium pada sistem Mg-Al akan membentuk partikel Mg17Al12 yang menyebabkan terjadinya grain refining pada matriks -Mg. Demikian pula, penambahan Zn dalam sistem Mg-Zn meningkatkan kekuatan dan kekerasan paduan. Oleh karena itu, penambahan gabungan Al dan Zn dalam sistem Mg-Al-Zn akan menarik untuk aplikasi komponen otomotif. Pada penelitian ini telah dilakukan proses pengecoran Mg-9Al-1Zn (wt. %) melalui gaya gravitasi pada cetakan logam dengan metode pendinginan udara. Paduan cor yang ditunjuk sebagai paduan Mg9Al1Zn mendapat perlakuan larutan pada suhu 415 C selama 2 jam. Pengamatan struktur mikro untuk paduan cor menunjukkan adanya -Mg sebagai matriks dengan fraksi terbesar dan fasa -Mg17Al12 sebagai endapan. Struktur mikro juga menunjukkan adanya pori-pori yang ditandai dengan warna hitam. Kami juga telah melakukan mikroanalisis untuk setiap fase yang ada dalam sampel dengan EDS yang mendeteksi semua elemen. Hasil evaluasi Kekerasan menegaskan bahwa solusi yang diperlakukan paduan as-cast memiliki nilai kekerasan 65,21. VHN meningkat secara signifikan jika dibandingkan dengan cast-alloy asli yang hanya 73,02 VHN. Peningkatan kekerasan dibahas dalam kaitannya dengan metode pengolahan dan pengembangan struktur mikro setelah perlakuan larutan.
......Magnesium alloys are lightweight materials that have a great potential to be developed because the alloy can reduce the energy consumption and total weight. The alloy is made of magnesium metal as a primary component characterized by a soft and mechanically lowstrength. The addition of aluminium in Mg-Al system will form Mg17Al12 particles causing grain refining the effect of the ?-Mg matrix. Similarly, the addition of Zn in Mg-Zn system increases the strength and hardness of the alloy. Hence, the combined addition of Al and Zn in Mg-Al-Zn system would be interesting for automotive component applications. In this study, we have carried out the casting process for Mg-9Al-1Zn (wt. %) through a gravity of the metal mold with air cooling method. The cast alloy designated as Mg9Al1Zn alloy received a solution treatment at temperature of 415 ?C for 2 hours. The microstructure observation for the cast alloy showed the presence of ?-Mg as a matrix with the largest fraction and ?-Mg17Al12 phase as a precipitate. The microstructure also showed the presence of pores indicated by black colour. We have also undertaken microanalysis to each phase present in the sample by EDS that detected all elements. The result of Hardness evaluation confirmed that the solution treated as-cast alloys possessed the hardness value of 65.21. The VHN significantly enhanced when compared with that of original cast-alloy which was only 73.02 VHN. The enhancement of the hardness is discussed in relation with processing method and microstructure development after a solution treatment. |
| 090 No. Panggil Setempat | MK-pdf |
| d-Entri Utama Nama Orang | |
| 500 Catatan Umum | |
| 337 Media Type | unmediated (rdacontent); computer (rdacontent) |
| d-Entri Tambahan Nama Orang | |
| 526 Catatan Informasi Program Studi | Fisika |
| 100 Entri Utama Nama Orang | Adi Ganda Putra, author |
| 264a Kota Terbit | Depok |
| 300 Deskripsi Fisik | 7 pages : illustrations ; 28 cm |
| 904a Pengisi Lembar Kerja | Aa |
| Akses Naskah Ringkas | |
| 856 Akses dan Lokasi Elektronik | |
| 502 Catatan Jenis Karya | Makalah dan Kertas Kerja |
| 041 Kode Bahasa | eng |