001 Hak Akses (open/membership)membership
700 Entri Tambahan Nama OrangSutrasno Kartohardjono, promotor; Meri Suhartini, co-promotor; Nelson Saksono, examiner; Yenny Meliana, examiner; Eva Fathul Karamah, examiner; Yuliusman, examiner
336 Content Typetext (rdacontent)
264b Nama PenerbitFakultas Teknik Universitas Indonesia
710 Entri Tambahan Badan KorporasiUniversitas Indonesia. Fakultas Teknik
504 Catatan Bibliografipages 91-92
049 No. Barkod07-23-18666724
852 LokasiPerpustakaan UI
338 Carrier Typeonline resource (rdacarrier)
590 Cat. Sumber Pengadaan Koleksi
903 Stock Opname
534 Catatan Versi Asli
Tahun Buka Akses2030
053 No. Induk07-23-18666724
653 Kata Kuncimembran selulosa asetat; kopolimerisasi cangkok; polietilen glikol metil eter akrilat; pemisahan gas CO2
040 Sumber PengataloganLibUI ind
245 Judul UtamaPencangkokan Polietilen Glikol Metil Eter Akrilat (PEGMEA) secara radiasi pada selulosa asetat untuk membran pemisah gas CO2/CH4 = Radiation Grafting of Polyethylene Glycol Methyl Ether Acrylate (PEGMEA) onto cellulose acetate for CO2/CH4 gas separation membranes
650 Subyek TopikGas separation membranes; Membranes (Technology)
264c Tahun Terbit2023
850 Lembaga PemilikUniversitas Indonesia
520 Ringkasan/Abstrak/IntisariStudi pemisahan gas CO2 dari CH4 penting dilakukan untuk meminimalisir efek negatif dari gas CO2 yang terkandung pada gas alam. Salah satu teknologi pemisahan yang banyak digunakan untuk pemisahan gas CO2 adalah teknologi membran. Tujuan dari penelitian ini adalah modifikasi membran CA menjadi fixed carrier membrane (FCM) dengan penambahan polietilen glikol (PEG) dan polietilen glikol metil eter akrilat (PEGMEA) sebagai zat aktif membran untuk meningkatkan permeabilitas gas CO2 pada membran. Produksi membran CA-PEGMEA dilakukan dengan proses mixing yang dilanjutkan dengan pemberian iradiasi sinar gamma secara simultan agar terjadi kopolimerisasi cangkok antara CA dan PEGMEA. Penambahan metilen bisakrilamida (MBA) pada studi awal dilakukan untuk mengetahui pengaruhnya terhadap sifat mekanik membran dan permeabilitas gas pada membran. Membran kemudian dikarakterisasi untuk mengetahui derajat kopolimerisasi (DC), perubahan struktur kimia (FTIR dan NMR), morfologi (SEM dan AFM), struktur kristal (XRD), serta kestabilan mekanik (UTM) dan termalnya (DSC). Metode Uji kinerja membran kemudian dilakukan terhadap gas murni CO2, gas murni CH4 dan gas campuran biner CO2 dan CH4. Uji karakterisasi DC menunjukkan bahwa nilai DC tertinggi terdapat pada membran CA-PEGMEA1(5), CA-PEGMEA3(15) dan CA-PEGMEA5(10). Hasil uji NMR menunjukkan adanya PEGMEA yang tercangkok pada polimer CA. Pada uji AFM ditunjukkan bahwa nilai kekasaran membran meningkat pada membran CA-PEGMEA dengan dosis iradiasi 5 kGy. Hasil analisis struktur kristal membuktikan kemungkinan bahwa PEG berinteraksi secara ikatan hidrogen dengan CA pada matriks polimer. Hasil uji kestabilan termal dan mekanik menunjukkan bahwa keberadaan MBA meningkatkan kestabilan termal dan mekanik, sedangkan pengaruh PEGMEA cenderung menurunkannya. Studi kinerja membran menunjukkan bahwa permeabilitas gas CO2 pada membran meningkat dengan adanya PEGMEA (dari 364 ke 679 barrer) yang tercangkok secara iradiasi pada membran, sedangkan pengaruh MBA justru menurunkan permeabilitas membran jika dibandingkan dengan membran CA-PEG tanpa MBA. Selektifitas ideal CO2/CH4 juga meningkat pada membran termodifikasi PEGMEA (dari 11 ke 48). Sementara itu hasil uji pemisahan gas binner CO2/CH4 menunjukkan bahwa fraksi mol CH4 pada retentate tertinggi didapatkan pada membran CA-PEGMEA1(5) dengan tekanan 40 Psi, yaitu 0,87. ......It is essential to study the separation of CO2 from CH4 to minimize the adverse effects of CO2 in natural gas. Membrane technology is one of the most widely used separation technologies for CO2 gas separation. This study aimed to modify the CA membrane to become a fixed carrier membrane (FCM) with the addition of polyethylene glycol (PEG) and polyethylene glycol methyl ether acrylate (PEGMEA) as active membrane agents to increase the permeability of CO2 gas in the membrane. Production of CA-PEGMEA membranes was done by a mixing process followed by simultaneous gamma-ray irradiation so that graft copolymerization occurs between CA and PEGMEA. The addition of methylene bisacrylamide (MBA) in the initial study was carried out to determine the effect on the membrane's mechanical properties and gas permeability. The membranes were then characterized to determine the degree of copolymerization (DC), changes in chemical structure (FTIR and NMR), morphology (SEM and AFM), crystal structure (XRD), and mechanical stability (UTM), and thermal (DSC). Methods The membrane performance test was then carried out on CO2 pure gas, CH4 pure gas, and a binary mixture of CO2 and CH4 gases. The DC characterization test showed that the highest DC values were found in CA-PEGMEA1(5), CA-PEGMEA3(15), and CA-PEGMEA5(10) membranes. The NMR test results confirmed the presence of PEGMEA grafted onto the CA polymer. The AFM test showed that the value of membrane roughness increased on the CA-PEGMEA membrane with an irradiation dose of 5 kGy. The results of the crystal structure analysis prove the possibility that PEG interacts by hydrogen bonding with CA in the polymer matrix. The results of the thermal and mechanical stability tests show that the presence of MBA increases the thermal and mechanical stability, the influence of PEGMEA tends to decrease it. Membrane performance studies showed that the CO2 gas permeability of the membrane increased in the presence of PEGMEA (from 364 to 679 barrer) grafted irradiated onto the membrane, while the effect of MBA decreased membrane permeability when compared to CA-PEG membranes without MBA. The ideal selectivity of CO2/CH4 also increased in PEGMEA-modified membranes (from 11 to 48). Meanwhile, the CO2/CH4 binary gas separation test results showed that the mole fraction of CH4 in the highest retentate was found in the CA-PEGMEA1(5) membrane with a pressure of 40 Psi, i.e., 0.87.
904b Pemeriksa Lembar KerjaSugiarti, Iyan-07-2024
090 No. Panggil SetempatD-pdf
d-Entri Utama Nama Orang
500 Catatan UmumTidak dapat diakses di UIANA, karena: akan ditulis dalam bahasa Inggris untuk dipersiapkan terbit pada Jurnal Internasional yaitu yang diprediksi akan dipublikasikan pada bulan tahun
337 Media Typecomputer (rdamedia)
d-Entri Tambahan Nama Orang
526 Catatan Informasi Program StudiTeknik Kimia
100 Entri Utama Nama OrangArifina Febriasari, author
264a Kota TerbitDepok
300 Deskripsi Fisikxv, 102 pages : illustration + appendix
904a Pengisi Lembar KerjaSugiarti-Oktokber-2023
Akses Naskah Ringkas
856 Akses dan Lokasi Elektronik
502 Catatan Jenis KaryaDisertasi
041 Kode Bahasaind