| 001 Hak Akses (open/membership) | membership |
| 700 Entri Tambahan Nama Orang | Ahmad Zakiyuddin, supervisor; Reza Miftahul Ulum, examiner; Alfian Ferdiansyah, examiner; Dwi Marta Nurjaya, examiner |
| 336 Content Type | text (rdacontent) |
| 264b Nama Penerbit | Fakultas Teknik Universitas Indonesia |
| 710 Entri Tambahan Badan Korporasi | Universitas Indonesia. Fakultas Teknik |
| 049 No. Barkod | 15-25-09733436 |
| 504 Catatan Bibliografi | pages 63-69 |
| 852 Lokasi | Perpustakaan UI |
| 338 Carrier Type | online resource (rdacarrier) |
| 590 Cat. Sumber Pengadaan Koleksi | Deposit;Deposit |
| 903 Stock Opname | |
| 534 Catatan Versi Asli | |
| Tahun Buka Akses | 2021 |
| 053 No. Induk | 15-25-09733436 |
| 653 Kata Kunci | konsentrat tembaga; korosi galvanik; sistem organik coating; electrochemical impedance spectroscopy (EIS); impedansi |
| 040 Sumber Pengatalogan | LibUI ind rda |
| 245 Judul Utama | Evaluasi Performa Organik Coating Pada Struktur Baja Karbon A36 di Lingkungan Konsentrat Tembaga Dengan Teknik Electrochemical Impedance Spectroscopy = Evaluation of Organic Coating Performance on Carbon Steel A 36 in Copper Concentrate Environment Using Electrochemical Impedance Spectroscopy |
| 264c Tahun Terbit | 2021 |
| 650 Subyek Topik | Organic coating; Carbon steel; Impedance spectroscopy |
| 850 Lembaga Pemilik | Universitas Indonesia |
| 520 Ringkasan/Abstrak/Intisari | Pabrik pengeringan konsentrat tembaga memiliki peranan penting sebagai tahap akhir dalam proses penambangan tembaga. Keberlangsungan operasi pabrik sangat dipengaruhi oleh kondisi bangunan dan fasilitas yang berbahan dasar baja. Persentase tembaga yang ada dalam konsentrat berkisar antara 20-40 %, Kalkopirit memiliki jumlah tembaga yang besar pada akhir ekstraksi. Pengaruh kehadiran kalkopirit dapat meningkatkan laju korosi pada baja melalui pasangan galvanik. pemilihan sistem coating untuk mellindungi baja menjadi penting dimana ketahanan material coating dipengaruhi oleh kekuatan terhadap cacat pada lapisan. Pada penelitian ini lima sistem organik coating yang diaplikasikan pada baja karbon A 36 dievaluasi kekuatannya terhadap korosi akibat kehadiran konsentrat tembaga dengan metode Electrochemical Impedance Spectroscopy (EIS), uji sembur garam dan uji tarik. Hasil pengujian menunjukkan bahwa sistem coating C2, C3, C4 dan C5 mempertahankan sifat penghalang yang baik selama proses perendaman, nilai impedansi |Z| pada frekuensi rendah lebih dari 108 ?.cm2 setelah 30 hari. Coating modifikasi epoksi (C1) memiliki impedansi terendah dengan resistansi di bawah 106 ?.cm2 memberikan perlindungan korosi yang buruk.
......The copper concentrate dewatering plant has an important role as a step end in the copper mining process. The continuity of plant operation is very influenced by the condition of buildings and facilities made of steel. Percentage of copper present in the copper concentrate is in the range of 20 to 40 %. Thus, Chalcopyrite is preferable to get large amount of copper at the end of the extraction. The presence of chalcopyrite increases the corrosion rate of carbon steel through a galvanic couple. Probably the most important step in coating selection is to evaluate the conditions under which the coating must perform. In this study, five organic coating systems were applied to A-36 steel and evaluated evaluated for their strength against galvanic corrosion in the presence of copper concentrate by electrochemistry impedance spectroscopy (EIS) measurement, salt spray test and pull off test. The test results showed that C2, C3, C4 and C5 coating systems maintained good barrier property during the immersion process, the impedance value |Z| at a low frequency are more than 108 ?.cm2 after 30 days in immersion exposure. Epoxy modified coating (C1) had the lowest impedance with resistance under 106 ?.cm2 providing poor corrosion protection. |
| 904b Pemeriksa Lembar Kerja | Amiarsih Indah Purwiati-Juli 2025 |
| 090 No. Panggil Setempat | T-pdf |
| d-Entri Utama Nama Orang | |
| 500 Catatan Umum | Dapat diakses di UIANA (lib.ui.ac.id) saja. |
| d-Entri Tambahan Nama Orang | |
| 337 Media Type | computer (rdamedia) |
| 526 Catatan Informasi Program Studi | Teknik Metalurgi dan Material |
| 100 Entri Utama Nama Orang | Ahmad Fauzi, author |
| 264a Kota Terbit | Depok |
| 300 Deskripsi Fisik | xiv, 69 pages : illustration + appendix |
| 904a Pengisi Lembar Kerja | Amiarsih Indah Purwiati-Juli 2025 |
| Akses Naskah Ringkas | |
| 856 Akses dan Lokasi Elektronik | |
| 502 Catatan Jenis Karya | Tesis |
| 041 Kode Bahasa | ind |