001 Hak Akses (open/membership)membership
700 Entri Tambahan Nama OrangDeni Ferdian, supervisor; Reza Miftahul Ulum, examiner; Ahmad Zakiyuddin, examiner; Adam Febriyanto Nugraha, examiner
336 Content Typetext (rdacontent)
264b Nama PenerbitFakultas Teknik Universitas Indonesia
710 Entri Tambahan Badan KorporasiUniversitas Indonesia. Fakultas Teknik
049 No. Barkod15-25-11354742
504 Catatan Bibliografipages 47-51
852 LokasiPerpustakaan UI
338 Carrier Typeonline resource (rdacarrier)
590 Cat. Sumber Pengadaan KoleksiDeposit;Deposit
903 Stock Opname
534 Catatan Versi Asli
Tahun Buka Akses2021
053 No. Induk15-25-11354742
653 Kata Kuncianoda korban; aluminium; logam tanah jarang; lantanum
040 Sumber PengataloganLibUI ind rda
245 Judul UtamaEfek Penambahan Lantanum pada Mikrostruktur dan Perilaku Korosi Anoda Korban Tegangan Rendah Al-Zn-Sn = Effect of Lanthanum on Microstructure and Corrosion Behavior of Al-Zn-Sn as a Low Voltage Sacrificial Anode for Marine Environment
264c Tahun Terbit2021
650 Subyek TopikCorrosion and anti-corrosives; Lanthanum
850 Lembaga PemilikUniversitas Indonesia
520 Ringkasan/Abstrak/IntisariSalah satu anoda korban yang paling banyak dipelajari adalah paduan Al-Zn-Sn, yang memiliki efisiensi arus sekitar 70%. Untuk meningkatkan efisiensi anoda korban paduan aluminium, logam tanah jarang seperti lantanum sering ditambahkan. Dari beberapa penelitian, penambahan logam tanah jarang menunjukkan efek yang berbeda, mulai dari peningkatan efisiensi arus hingga sealing effect pada lapisan pasif. Oleh karena itu, diperlukan penelitian lebih lanjut mengenai pengaruhnya terhadap struktur mikro dan sifat korosi dari penambahan lantanum pada salah satu paduan aluminium yang sering digunakan, seperti Al-Zn-Sn. Variasi sampel uji adalah Al-Zn-0.5Sn-xLa dan Al-Zn-1Sn-xLa (x= 0,1; 0,3; 0,5). Sampel akan diuji mikroskop optik, SEM-EDS, polarisasi siklik, EPMA dan EIS. Dari pemetaan unsur dengan EDS dan EPMA, lantanum terdistribusi dalam matriks Al dan presipitat dengan membentuk senyawa intermetalik Al11La3. Hasil OCP menunjukkan penurunan seiring dengan peningkatan lantanum. Hasil OCP sekitar -1,2 V dimana hasil tersebut lebih tinggi dari OCP anoda korban tegangan rendah yaitu -0.85 vs SCE. Dari hasil polarisasi siklik, potensi pitting corrosion terlihat menurun seiring dengan meningkatnya konsentrasi lantanum. Dari hasil EIS, resistansi transfer muatan meningkat seiring dengan penambahan konsentrasi lantanum. Dari hasil pengujian tersebut, paduan Al-Zn-Sn-La tidak dapat diklasifikasikan sebagai anoda korban tegangan rendah. ......One of the most studied sacrificial anodes is the Al-Zn-Sn alloy, which has a current efficiency of about 70%. To increase the efficiency of aluminium alloy sacrificial anodes, rare earth metals such as lanthanum are often added. From several studies, the addition of rare earth metals shows different effects, from increasing current efficiency until sealing effect on passive layer. Therefore, further research is needed on the effects on microstructure and corrosion properties of adding lanthanum to one of the frequently used aluminium alloys, such as Al-Zn-Sn. The variations of the test samples were Al-Zn-0.5Sn-xLa and Al-Zn-1Sn-xLa (x= 0.1, 0.3, 0.5). The samples were tested for optical microscope, SEM-EDS, EPMA cyclic polarization and EIS. From mapping from EDS and EPMA, lanthanum was distributed in Al matrix and precipitate by forming an intermetallic compound ?Al11La3. OCP result shown decreasing as lanthanum increases. OCP result is about -1.2 V that higher than low voltage sacrificial anode OCP (-0.85V vs SCE). From the cyclic polarization result, potential of pitting corrosion was shown decreasing as the lanthanum concentration increased. Charge transfer resistance shown increasing as lanthanum concentration is increasing in EIS result. Therefore, Al-Zn-Sn-La cannot be classified as low voltage sacrificial anode.
904b Pemeriksa Lembar KerjaAmiarsih Indah Purwiati-Juli 2025
090 No. Panggil SetempatT-pdf
d-Entri Utama Nama Orang
500 Catatan UmumTidak dapat diakses di UIANA, karena: akan ditulis dalam bahasa Inggris dan dipresentasikan sebagai makalah pada Seminar Internasional yaitu Corrosion Science
d-Entri Tambahan Nama Orang
337 Media Typecomputer (rdamedia)
526 Catatan Informasi Program StudiTeknik Metalurgi dan Material
100 Entri Utama Nama OrangDony Prasetya, author
264a Kota TerbitDepok
300 Deskripsi Fisikxiii, 51 pages : illustration + appendix
904a Pengisi Lembar KerjaAmiarsih Indah Purwiati-Juli 2025
Akses Naskah Ringkas
856 Akses dan Lokasi Elektronik
502 Catatan Jenis KaryaTesis
041 Kode Bahasaind