700 Entri Tambahan Nama OrangMuhammad Ridwan, supervisor; Changsoo Kim, supervisor; Ivandini Tribidasari Anggraningrum, examiner; Aminah, examiner
001 Hak Akses (open/membership)membership
336 Content Typetext (rdacontent)
710 Entri Tambahan Badan KorporasiUniversitas Indonesia. Fakultas Matematika dan Ilmu Pengetahuan Alam
264b Nama PenerbitFakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia
504 Catatan Bibliografipages 65-76
049 No. Barkod14-25-34567771
852 LokasiPerpustakaan UI
338 Carrier Typeonline resource (rdacarrier)
590 Cat. Sumber Pengadaan KoleksiDeposit
903 Stock Opname
534 Catatan Versi Asli
Tahun Buka Akses2028
053 No. Induk14-25-34567771
653 Kata KunciH2 energy; methanol steam reforming; Cu-based catalyst; CaCe(x)Zr(1-x)O3 support; cerium-zirconium
040 Sumber PengataloganLibUI ind rda
245 Judul UtamaEfek Rasio Ce-Zr terhadap Aktivitas Katalitik Cu/CaCe(x)Zr(1-x)O3 pada Reaksi Methanol Steam Reforming untuk Produksi H2 = The Effect of Ce-Zr Ratio on the Catalytic Activity of Cu/CaCe(x)Zr(1-x)O3 in the Methanol Steam Reforming Reaction for H2 Production
650 Subyek TopikMethanol; Cerium; Zirconium; Hydrogen
264c Tahun Terbit2025
850 Lembaga PemilikUniversitas Indonesia
520 Ringkasan/Abstrak/IntisariSektor energi menjadi penyumbang 75% emisi gas rumah kaca yang dilaporkan oleh International Energy Agency tahun 2021. Oleh karena itu, transisi penggunaan energi fosil ke energi alternatif, salah satunya energi hidrogen (H2), harus diimplementasikan lebih luas lagi terutama terhadap kedua sektor tersebut untuk mengurangi emisi gas rumah kaca. Penelitian ini bertujuan untuk mengembangkan katalis berbasis tembaga (Cu) yang tinggi aktivitas katalitiknya pada reaksi methanol steam reforming (MSR) untuk memproduksi H2. Pemilihan support yang baik penting untuk performa katalis Cu. Dalam penelitian ini, Ce diperkenalkan sebagai dopan Zr pada sistem support CaZrO3. CeO2 dikenal sebagai support sekaligus promoter yang baik karena karakteristik oxygen storage capacity (OSC) yang tinggi sehingga dapat meningkatkan aktivitas katalitik Cu/CaCe(x)Zr(1-x)O3. Cu/CaCe(x)Zr(1-x)O3 disintesis dengan metode sol-gel dan dry impregnation dan diuji aktivitasnya pada reaksi MSR pada 250, 300, dan 350 °C. Komposisi Ce-Zr dan variabel temperatur dievaluasi pada penelitian ini. Cu/CaCe(x)Zr(1-x)O3 dikarakterisasi dengan XRF, XRD, Spektroskopi Raman, SAA, O2-TPO, dan TEM. Hasilnya, variasi rasio Ce-Zr telah sesuai dengan yang diharapkan, Cu telah berhasil diimpregnasi ke permukaan support, kelima katalis adalah material mesopori, dan Cu/CaCeO3 diketahui memiliki densitas oxygen vacancy (Ovac) tertinggi, yang menandakan OSC yang juga tinggi. Sesuai dengan perolehan densitas Ovac tertinggi, Cu/CaCeO3 unggul dalam uji reaksi MSR di ketiga temperatur uji, dengan konversi metanol, yield H2, dan produksi H2 pada temperatur tertinggi berturut-turut sebesar 98,37%, 86,59%, dan 0,0539 mol/min/gcat. ......The energy sector accounted for 75% of greenhouse gas emissions reported by the International Energy Agency in 2021. Therefore, the transition from fossil fuels to alternative energy sources, one of which is hydrogen (H?) energy, must be widely implemented especially in those two sectors to reduce greenhouse gas emissions. This research aims to develop a copper (Cu)-based catalyst with high catalytic activity in the methanol steam reforming (MSR) reaction for H2 production. The selection of a suitable support is crucial for the performance of the Cu-based catalysts. In this study, Ce is introduced as a dopant in Zr within the CaZrO3 support system. CeO? is well-known to be an excellent support and promoter due to its high oxygen storage capacity (OSC) characteristic, which can enhance the catalytic activity of Cu/CaCe(x)Zr(1-x)O3. Cu/CaCe(x)Zr(1-x)O3 was synthesized using sol-gel and dry impregnation methods and tested for activity in the MSR reaction at temperatures of 250, 300, and 350 °C. The Ce-Zr composition and temperature variables are evaluated in this study. Cu/CaCe(x)Zr(1-x)O3 was characterized using XRF, XRD, Raman spectroscopy, SAA, O2-TPO, dan TEM. The results indicate that the desired and obtained ratios of the catalyst are in agreement with one another, Cu is successfully impregnated onto the surface of CaCe(x)Zr(1-x)O3, all five catalysts are mesoporous materials, and Cu/CaCeO3 exhibits the highest density of oxygen vacancies (Ovac), indicating a high OSC. Consistent with the highest Ovac density obtained, Cu/CaCeO3 excels in MSR reaction tests at all three test temperatures, with methanol conversion, H? yield, and H? production at the highest temperature being 98,37%, 86,59%, dan 0,0539 mol/min/gcat.
904b Pemeriksa Lembar KerjaAmiarsih Indah Purwiati-Maret 2024
090 No. Panggil SetempatS-pdf
d-Entri Utama Nama Orang
500 Catatan UmumTidak dapat diakses di UIANA, karena: akan ditulis dalam bahasa Inggris untuk dipersiapkan terbit pada Jurnal Internasional yaitu International Journal of Hydrogen Energy yang diprediksi akan dipublikasikan pada bulan Juni tahun 2028
337 Media Typecomputer (rdamedia)
d-Entri Tambahan Nama Orang
526 Catatan Informasi Program StudiKimia
100 Entri Utama Nama OrangSintesa Ulfah, author
264a Kota TerbitDepok
300 Deskripsi Fisikxvi, 76 pages : illustration + appendix
904a Pengisi Lembar KerjaAmiarsih Indah Purwiati-Maret 2024
Akses Naskah Ringkas
856 Akses dan Lokasi Elektronik
502 Catatan Jenis KaryaSkripsi
041 Kode Bahasaind