| 700 Entri Tambahan Nama Orang | Ariadne Lakshmidevi Juwono, supervisor; Seto Roseno, supervisor; Vivi Fauzia, examiner; Suhardjo Poertadji, examiner |
| 001 Hak Akses (open/membership) | membership |
| 336 Content Type | text (rdacontent) |
| 710 Entri Tambahan Badan Korporasi | Universitas Indonesia. Fakultas Matematika dan Ilmu Pengetahuan Alam |
| 264b Nama Penerbit | Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia |
| 504 Catatan Bibliografi | pages 36-43 |
| 852 Lokasi | Perpustakaan UI |
| 049 No. Barkod | 14-25-92768597 |
| 338 Carrier Type | online resource (rdacarrier) |
| 590 Cat. Sumber Pengadaan Koleksi | Deposit |
| 903 Stock Opname | |
| 534 Catatan Versi Asli | |
| Tahun Buka Akses | 2025 |
| 053 No. Induk | 14-25-92768597 |
| 653 Kata Kunci | epoxy; kenaf fiber; nanocellulose; pineapple leaf fiber; polyurethane foam; sandwich composite; VARI |
| 040 Sumber Pengatalogan | LibUI ind rda |
| 245 Judul Utama | Pengaruh Fraksi Berat Selulosa Nanofibril Serat Kenaf Busa Poliuretan Terhadap Karakteristik Mekanik Komposit Sandwich Serat Nanas Subang/Epoksi = The Effect of Cellulose Nanofibril Weight Fraction Kenaf Fiber in Polyurethane Foam on the Mechanical Properties of Subang Pineapple Fiber/Epoxy Sandwich Composites |
| 650 Subyek Topik | Polyurethanes; Earthquake resistant design |
| 264c Tahun Terbit | 2024 |
| 850 Lembaga Pemilik | Universitas Indonesia |
| 904b Pemeriksa Lembar Kerja | Amiarsih Indah Purwiati-Mei 2025 |
| 520 Ringkasan/Abstrak/Intisari | Indonesia merupakan negara yang sering terjadi gempa bumi, sehingga pengembangan material konstruksi tahan gempa menjadi sangat penting. Di sisi lain, limbah pertanian seperti serat daun nanas (PALF) memiliki postensi besar untuk dimanfaatkan. Penelitian ini bertujuan untuk menentukan sifat mekanik komposit sandwich epoksi yang diperkuat serat daun nanas (PALF) sebagai skin dan busa poliuretan (PU) yang diperkuat selulosa nanofibril (CNF) serat kenaf sebagai core. Komposit skin (EP/PALF) difabrikasi dengan metode VARI (Vacuum Assested Resin Infusion). Sedangkan EP/PALF dan PU serta PU/1wt CNF, PU/3wt CNF, dan PU/5wt CNF digabungkan dengan metode cold press. Hasil pengujian menunjukkan bahwa penambahan CNF pada core busa PU meningkatkan kekuatan tekan hingga mencapai (4,88 ± 0,62) MPa dan modulus tekan sebesar (14,01 ± 1,95) MPa pada EP/PALF-PU/5wt CNF. EP/PALF-PU memiliki nilai tarik dan lentur tertinggi yaitu masing-masing sebesar (0,15 ± 0,09) MPa dan (7,79 ± 0,34) MPa. Penambahan CNF menurunkan kinerja tarik dan lentur EP/PALF-PU akibat aglomerasi dan void yang tidak merata. Dengan demikian, formulasi CNF pada busa PU terbukti efektif dalam meningkatkan sifat tekan.
......Indonesia is a country frequently affected by earthquakes, making the development of earthquake-resistant construction materials highly essential. On the other hand, agricultural waste such as pineapple leaf fiber (PALF) holds significant potential for utilization. This study aimed to determine mechanical properties of an epoxy sandwich composite reinforced with pineapple leaf fiber (PALF) as the skin and polyurethane (PU) foam reinforced with cellulose nanofibrils (CNF) from kenaf fiber as the core. The skin composites (EP/PALF) were fabricated using the Vacuum Assisted Resin Infusion (VARI) method, while the EP/PALF skin and PU foam core ? including PU/1wt CNF, PU/3wt CNF, and PU/5wt CNF- were constructed using the cold press method. The results showed that the addition of CNF to the PU foam core increased the compressive strength to (4,88 ± 0,62) MPa at EP/PALF-PU/5wt CNF. Moreover, the highest tensile and flexural strengths were observed at EP/PALF-PU, with the values of (0,15 ± 0,09) MPa and (7,79 ± 0,35) MPa, respectively, while the addition of CNF in PU reduced the tensile and flexural performance due to agglomeration and uneven void distribution. Thus, the CNF formulation in PU foam has proven effective in enhancing compressive properties. |
| 090 No. Panggil Setempat | S-pdf |
| d-Entri Utama Nama Orang | |
| 500 Catatan Umum | Tidak dapat diakses di UIANA, karena: akan ditulis dalam bahasa Inggris untuk dipersiapkan terbit pada Jurnal Internasional yaitu AIP Advances yang diprediksi akan dipublikasikan pada bulan September tahun 2025 |
| 337 Media Type | computer (rdamedia) |
| d-Entri Tambahan Nama Orang | |
| 526 Catatan Informasi Program Studi | Fisika |
| 100 Entri Utama Nama Orang | Rizqi Akmalia Jailani, author |
| 264a Kota Terbit | Depok |
| 300 Deskripsi Fisik | xiv, 43 pages : illustration |
| 904a Pengisi Lembar Kerja | Amiarsih Indah Purwiati-Mei 2025 |
| Akses Naskah Ringkas | |
| 856 Akses dan Lokasi Elektronik | |
| 502 Catatan Jenis Karya | Skripsi |
| 041 Kode Bahasa | ind |