| 001 Hak Akses (open/membership) | membership |
| 700 Entri Tambahan Nama Orang | Azwar Manaf, supervisor; Budhy Kurniawan, examiner; Ferry Anggoro Ardy Nugroho, examiner |
| 336 Content Type | text (rdacontent) |
| 264b Nama Penerbit | Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia |
| 710 Entri Tambahan Badan Korporasi | Universitas Indonesia. Fakultas Matematika dan Ilmu Pengetahuan Alam |
| 504 Catatan Bibliografi | pages 44-47 |
| 049 No. Barkod | 14-25-06552787 |
| 852 Lokasi | Perpustakaan UI |
| 338 Carrier Type | online resource (rdacarrier) |
| 590 Cat. Sumber Pengadaan Koleksi | Deposit;Deposit |
| 903 Stock Opname | |
| 534 Catatan Versi Asli | |
| Tahun Buka Akses | 2025 |
| 053 No. Induk | 14-25-06552787 |
| 653 Kata Kunci | nanokomposit; material magnetik; reduksi; penyerapan gelombang mikro; nanocomposites; magnetic materials; reduction; microwave absorption |
| 040 Sumber Pengatalogan | LibUI ind rda |
| 245 Judul Utama | Rekayasa Kemagnetan dan Penyerapan Gelombang Mikro pada Nanokomposit SHF-FeCo melalui Reduksi Karbon CoFe2O4 = Magnetic Engineering and Microwave Absorption in SHF-FeCo Nanocomposites through Carbon Reduction of CoFe2O4 |
| 264c Tahun Terbit | 2024 |
| 650 Subyek Topik | Magnetic engineering; Microwave absorption; Nanocomposites (Materials) |
| 850 Lembaga Pemilik | Universitas Indonesia |
| 520 Ringkasan/Abstrak/Intisari | Penelitian ini dilakukan untuk membuat material nanokomposit magnetik berbahan dasar stronsium heksaferit (SrFe12O19 atau SHF) dan besi kobalt (FeCo) sebagai Radar Absorbing Material (RAM). Telah dibuat nanokomposit (SrFe12O19)1-x.(FeCo)x melalui metode mechanical milling dengan variasi x=0; 0.3 dan 0.5. Komposit dibuat menggunakan nano SHF dan paduan FeCo. FeCo diperoleh dari reduksi karbon nano CoFe2O4 pada temperatur 1100°C selama 3 dan 5 jam disertai dengan quenching. Karakterisasi magnet diambil dengan pengujian Permagraf dan VSM. Karakterisasi fasa didapatkan dengan uji XRD. Pengujian VNA dilakukan untuk mendapat nilai reflection loss (RL) sehingga dapat diketahui persentase serapan nanokomposit yang terbentuk.
......This research purpose is to make a magnetic nanocomposite material based on strontium hexaferrite (SrFe12O19 or SHF) and iron-cobalt (FeCo) as a Radar Absorbing Material (RAM). Nanocomposites following the composition of (SrFe12O19)1-x.(FeCo)x through mechanical milling method with x=0; 0,3 and 0,5 has been made. The composites are based on nano SHF and FeCo alloy. The FeCo alloy was synthesized via carbon reduction of nano CoFeâ‚‚Oâ‚„ in 1100°C with various holding time of 3 and 5 hours, with quenching applied after annealing. Magnetic characterization was gained through Permagraph and VSM testing. The phases of the nanocomposites gained through XRD testing. VNA testing was done to gain reflection loss (RL) value so the absorbtion percentage of the created nanocomposite can be calculated. |
| 904b Pemeriksa Lembar Kerja | Amiarsih Indah Purwiati-Februari 2024 |
| 090 No. Panggil Setempat | S-pdf |
| d-Entri Utama Nama Orang | |
| 500 Catatan Umum | Dapat diakses di UIANA (lib.ui.ac.id) saja. |
| 337 Media Type | computer (rdamedia) |
| d-Entri Tambahan Nama Orang | |
| 526 Catatan Informasi Program Studi | Fisika |
| 100 Entri Utama Nama Orang | Dinda Syifa Hamidah, author |
| 264a Kota Terbit | Depok |
| 300 Deskripsi Fisik | xiv, 47 pages : illustration |
| 904a Pengisi Lembar Kerja | Amiarsih Indah Purwiati-Februari 2024 |
| Akses Naskah Ringkas | |
| 856 Akses dan Lokasi Elektronik | |
| 502 Catatan Jenis Karya | Skripsi |
| 041 Kode Bahasa | ind |