Pengaruh pengelasan metoda SMAW & GTAW terhadap perilaku korosi austenitic stainless steel 316L = effect of SMAW & GTAW methods to corrosion behavior in the welded austenitic stainless steel 316L plates

RR Reni Indraswari; Johny Wahyuadi Soedarsono, supervisor; Winarto, supervisor; Dedi Priadi, examiner; Andi Rustandi, examiner (Fakultas Teknik Universitas Indonesia, 2010)

 Abstrak

Baja tahan karat jenis austenitik tipe 316L banyak digunakan di berbagai industri. Untuk menyambungkan antar pipa dilakukan pengelasan, akan tetapi dalam penggunaannya sering terjadi korosi pada sambungan lasnya. Pada penelitian ini dilakukan pengelasan pada logam SS 316L dengan ukuran 150 mm x 300 mm, tebal 1,5 mm dan 3 mm. Metoda pengelasan yang dilakukan adalah SMAW and GTAW dengan variasi jenis filler (ER316L dan TGX-R316LT1-5) dan penggunaan gas back purging/shielding argon. Gas pelindung yang digunakan untuk metoda GTAW adalah argon murni.
Setelah proses pengelasan, akan dilakukan beberapa pengujian seperti pengujian kekerasan, metallografi untuk melihat struktur mikro serta pengujian ketahanan pitting. Pengujian dilakukan dengan membedakan spesimen yang dipreparasi dan yang tidak dipreparasi sebelum dilakukan pengujian dengan mencelupkan ke dalam larutan ferric cholride.
Hasil dari penelitian ini yaitu data pengujian kekerasan yang menunjukkan bahwa daerah Weld Metal memiliki kekerasan yang paling tinggi dari daerah lainnya dan dari pengamatan struktur mikro ditemukan adanya presipitasi karbida. Pada pengelasan baja tahan karat jenis ini juga ditemukan adanya oksida-oksida permukaan karena temperatur tinggi dan fenomena sensitisasi yang tidak lepas mempengaruhi ketahanan korosi, khususnya korosi pitting.

Austenitic Stainless Steel type 316L is mostly used in various industries. Usually, joining between the pipes by welding. Although on the use often happened corrosion failure on the weld joint.
This research use SS316L materials with size 150 mm x 300 mm, thickness 1,5 mm dan 3 mm. Methods welding are SMAW and GTAW with variation in filler metals (ER316L and TGX-R316LT1-5) and using gas back purging/shielding. Than, will be researched by hardness test and metallography test to know microstructure and pitting resistance test. Tests carried out by distinguishing specimens that are not prepared and prepared prior to testing by dipping into a solution of ferric chloride.
The result of this analysis, hardness test which show that Weld Metal zone is the hardest from the other. From the microsturcture analize show carbide precipitation. In welding stainless steel types are also found the existence of surface oxides due to high temperature and sensitization phenomena that can?t be separated affecting corrosion resistance, particularly pitting corrosion.

 Metadata

Jenis Koleksi : UI - Tesis Open
No. Panggil : T27966
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2010
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 64 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T27966 15-19-153838105 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 135527
Cover