Modifikasi zeolit alam Lampung dengan fotokatalitis TiO2 melalui metode sol gel untuk penyisihan fenol = Modification of Lampung's natural zeolite with titania photocalys prepared by sol gel method for phenol removal

Meta Ellyana; Slamet, supervisor (Fakultas Teknik Universitas Indonesia, 2007)

 Abstrak

Perkembangan teknologi dan perindustrian di Indonesia menyebabkan masalah pencemaran lingkungan karena limbah. Fenol merupakan polutan berbahaya yang banyak dijumpai dalam limbah-limbah industri. Oleh karena itu, dikembangkan metode pengolahan limbah yang mengkombinasikan proses adsorbsi dengan proses fotokatalitik. Berkaitan dengan hal tersebut maka dalam penulisan skripsi ini dilakukan modifikasi zeolit alam Lampung dengan fotokatalis TiO2 melalui metode sol gel untuk penyisihan fenol. Zeolit alam Lampung yang sudah mengalami treatment dilapisi dengan fotokatalis TiO2 yang dibuat sendiri mengunakan prekursor [Ti(OPr)4 AcAc]. Material adsorben fotokatalis terintegrasi (AFT) tersebut kemudian dikarakterisasi dengan BET dan XRF. Uji kinerja material AFT dalam menyisihkan fenol dilakukan dalam fotoreaktor yang dilengkapi 6 lampu UV jenis black lamp @ 10 watt dengan intensitas 162 mW/cm2 dan pengaduk mekanik. Analisis sampel fenol dilakukan dengan UV-VIS spectrophotometer. Dalam penelitian ini dilakukan variasi kandungan TiO2 pada AFT, variasi konsentrasi AFT dalam limbah fenol dan variasi konsentrasi awal fenol.
Diperoleh kandungan TiO2 dalam AFT yang optimum sebesar 15 % dan konsentrasi AFT dalam limbah fenol yang optimum dalam menyisihkan fenol 10 ppm sebesar 5 g/L. Penggunaan adsorben sebagai penyangga dapat meningkatkan penyisihan fenol yang terjadi, dibuktikan dari penyisihan fenol oleh ZAL 5 H-TiO2 lebih besar dari penyisihan fenol oleh Quartz-TiO2 15 %. Laju reaksi fotodegradasi meningkat dengan meningkatnya konsentrasi AFT dalam limbah dan konsentrasi awal fenol. Laju reaksi fotodegradasi oleh AFT dapat dimodelkan menggunakan mekanisme Langmuir Hinselwood. Kandungan TiO2 pada AFT memegang peranan penting dalam kinerja AFT menyisihkan fenol. Dengan mengkombinasikan adsorben dengan fotokatalis diperoleh metode pengolahan limbah yang lebih efektif dan efisien. Laju reaksi fotodegradasi juga dipengaruhi oleh konsentrasi AFT dalam limbah dan konsentrasi awal fenol.

Development of technology and industry in Indonesia has made environmental issue. Phenol is the hazardous organic pollutant in industrial waste. Therefore, combination of adsorption and photocatalytic process has developed. Because of that, in this thesis Lampung's natural zeolite was modified with photocatalyst TiO2 through sol gel method to remove phenol. Lampung's natural zeolite was activated by dealumination, then this zeolite was used as TiO2 support. The photocatalyst TiO2 was prepared by sol gel method using the titanium isopropoxide bis acetyl acetonate [Ti(OPr)4 AcAc] precursor. The zeolite loaded TiO2 is called as integrated adsorbent photocatalyst (IAP). IAP was characterized with BET and XRF. Photodegradation of phenol by IAP were carried out using a pyrex reactor (10 cm diameter) equipped with 6 UV lamp (@10 watt with intensity 162 mW/cm2 ) and mechanic stirrer. Phenol samples were analyzed with UVVis spectrophotometer.
This research study the effect of TiO2 loading in IAP, the effect of IAP concentration in waste and effect of phenol initial concentration. The optimum TiO2 loading in IAP is 15 % and the optimum IAP concentration to eliminate 10 ppm phenol is 5g/L. By using adsorbent as photocatalyst support, the elimination of phenol is increase from 58 % to 88 %. Photodegradation reaction rate is increasing with the increace IAP concentration in waste and phenol initial concentration. This reaction rate can be modeled using Langmuir Hinselwood mechanism. TiO2 loading in IAP hold important role in the performance of IAP to remove phenol. By combination of adsorbent and photocatalyst, more effective and efficient method to eliminate industrial waste is gotten. The photodegradation reaction rate was influenced by the concentration of IAP in waste and phenol initial concentration.

 File Digital: 1

Shelf
 S49770-Meta Ellyana.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S49770
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2007
Bahasa : ind
Sumber Pengatalogan :
Tipe Konten :
Tipe Media :
Tipe Carrier :
Deskripsi Fisik : xii, 57 hlm.; ill.; 30 cm. + lamp.
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S49770 14-22-94374244 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20247497
Cover