Karakterisasi Nanokristalin ZnO hasil Presipitasi dengan perlakuan pengeringan,anil dan pasca-hidrotermal

Ary Witjaksono; Akhmad Herman Yuwono, supervisor; Anne Zulfia, examiner; Sotya Astuningsih, examiner; Nofrijon Sofyan, examiner ([Publisher not identified] , 2011)

 Abstrak

ABSTRAK
Telah disintesis nanopartikel ZnO melalui metoda presipitasi dimana prekursor Zinc acetate dihydrate dilarutkan dalam etanol disertai pengadukan dan pemanasan. Variasi konsentrasi katalis NaOH sebesar 0.10, 0.175 dan 0.25 M serta perlakuan lanjut pengeringan, anil (variasi waktu tahan 12, 24 dan 48 jam pada temperatur konstan 150oC) dan pasca-hidrotermal dilakukan untuk mengetahui pengaruhnya terhadap pertumbuhan nanokristalit ZnO. Metode pengujian ultraviolet visible (UV-Vis) dan difraksi sinar-X (XRD) diterapkan guna kepentingan analisis terhadap sampel. dengan penilitian ini diharapkan diperoleh pengkayaan sebagai masukan dalam pencapaian parameter yang optimum bagai riset-riset selanjutnya. Dari hasil pengujian XRD, diperoleh bahwa pemberian perlakuan lanjut anil pada temperatur 150oC selama 24 jam mampu memberikan ukuran kristalit ZnO paling maksimal mencapai 23.23 nm.

ABSTRACT
Zinc oxide (ZnO) nanoparticles have been synthesized through precipitation, where zinc acetate dehydrate precursor was dissolved in ethanol assisted by stirring and heating processes. Variation in sodium hydroxide (NaOH) catalyst from 0.10, 0.175 and 0.25 M, and further treatments with drying, annealing (with variation of holding time for 12, 24 and 48 hours at constant temperature of 150oC) and post-hydrothermal have been performed in order to investigate the effects on the growth of ZnO nanocrystallites. For analysis purposes, x-ray diffraction and UV-Vis spectroscopy were performed on the resulting ZnO nanoparticles. The current work was aimed at putting a basic milestone for further research. On the basis of XRD analysis, it was known that the annealing process at 150oC for 24 hours can provide the biggest crystallite size for ZnO nanoparticles of 23.23 nm.

 File Digital: 1

Shelf
 T30253 - Karakterisasi nanokristalin.pdf :: Unduh

 Kata Kunci

 Metadata

Jenis Koleksi : UI - Tesis Open
No. Panggil : T30253
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2011
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 80 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T30253 T30253 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20298424
Cover