Studi pemisahan campuran Azeotrop Etanol-air dan Isopropil Alkohol-air melalui proses Pervaporasi dengan membran Thin Film Composite komersial

Ika Wahyuni; Setijo Bismo, supervisor; Sutrasno Kartohardjono, supervisor; Mohammad Nasikin, examiner; Nelson Saksono, examiner; Donni Adinata, examiner ([Publisher not identified] , 2012)

 Abstrak

ABSTRAK
Tesis ini membahas mengenai proses pemisahan dua jenis campuran
alkohol, yaitu campuran etanol-air dan isopropil alkohol-air (IPA-air), melalui
proses pervaporasi dengan menggunakan membran Thin Film Composite (TFC)
komersial. Pengaruh temperatur umpan, konsentrasi umpan, dan tekanan pada sisi
permeat diinvestigasi berkaitan dengan kinerja membran TFC komersial dalam
proses pervaporasi tersebut. Untuk penentuan kondisi operasi, percobaan
pervaporasi dilakukan pada temperatur umpan 35, 39, 44 °C dan tekanan pada sisi
permeat sebesar 660, 510, 260 mmHg-a. Hasil studi menunjukkan bahwa untuk
proses pervaporasi campuran etanol-air, kondisi operasi yang terbaik adalah pada
temperatur umpan dan tekanan sisi permeat masing-masing 39°C dan 510 mmHg,
dengan nilai fluks dan selektivitas masing-masing 0,085 kg/m2.mnt dan 1,075.
Sedangkan untuk proses pervaporasi campuran IPA-air, kondisi operasi yang
terbaik adalah pada temperatur umpan dan tekanan sisi permeat masing-masing 39
°C dan 260 mmHg, dengan nilai fluks dan selektivitas masing-masing 0,0098
kg/m2.mnt dan 1,361. Lebih lanjut, dilakukan percobaan PV campuran azeotrop
etanol-air dan IPA-air pada kondisi operasi optimum yang telah diperoleh
sebelumnya. Hasil percobaan menunjukkan bahwa membran TFC hanya dapat
menurunkan konsentrasi etanol di permeat dari 95,5 menjadi 94,3 %-b dan
konsentrasi IPA dari 85,7 menjadi 83,5 %-b. Berdasarkan hasil tersebut, agar
dapat dimanfaatkan sebagai membran pervaporasi, maka membran TFC harus
direkayasa secara khusus dalam proses pembuatannya.

ABSTRACT
The separation of two alcohol mixtures, which are ethanol-water and
isopropyl alcohol-water (IPA-water) mixtures, through pervaporation process by
commercial Thin Film Composite (TFC) membrane is discussed in this thesis.
Effect of feed temperature, downstream pressure, and feed composition are
investigated regarding the performance of TFC membrane in the pervaporation
process. A preliminary study was performed at various feed temperatures (35 ? 44
°C) and downstream pressures (660, 510, 260 mmHg-a), to determine the
optimum operational condition. The result showed that the optimum operating
condition for the pervaporation of ethanol-water mixture was at 39 °C and 510
mmHg-a, with the value of permeate flux and selectivity, which were about 0.085
kg/m2.min and 1.075. While the optimum operating condition for the
pervaporation IPA-water mixture was at 39 °C and 260 mmHg-a, with the value
of permeate flux and selectivity, which were about 0.0098 kg/m2.min and 1.361.
Furthermore, the pervaporation of ethanol-water and IPA-water azeotrope
mixtures were done by utilizing the optimum operational condition from the
previous study. The ethanol and IPA concentration in permeate obtained
decreased from 95.5 and 85.7 % to 94.3 and 83.5 %-b, respectively. While, their
concentration in retentate increased to 96.3 and 87.9 %-b.

 File Digital: 1

 Kata Kunci

 Metadata

Jenis Koleksi : UI - Tesis Open
No. Panggil : T30639
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2012
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 103 pages ; 28 cm. + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T30639 15-18-920683712 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20302326
Cover