Efek subtitusi bismuth (Bi) pada bahan La1-xBixMnO3 terhadap serapan gelombang elektromagnetik melalui proses paduan mekanik = Effect of subtituting bismuth (Bi) into La1-xBixMnO3 for its characterization of electromagnetic waves absorption through mechanical alloying process

Donny Iwansa; Budhy Kurniawan, supervisor; Azwar Manaf, examiner; Muhammad Hikam, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2012)

 Abstrak

Telah dilakukan pembuatan material La1-xBixMnO3 melalui proses paduan mekanik. Pembuatan material ini dibatasi oleh variasi dari pendopingan Bismuth (Bi) yang diberikan dengan nilai variasi x sebesar 0.05, 0.15, 0.20, 0.25 dan 0.35. Sampel ini kemudian dikarakterisasi menggunakan XRD (X-Ray Diffractometer) dan VNA (Vector Network Analyzer) untuk mengetahui sistem dan struktur kristal yang terbentuk dan mendapatkan nilai dari serapan gelombang elektromagnetik (rentang 9-15GHz) yang terdapat pada material ini, secara berurutan.
Hasil karakterisasi kemudian diolah untuk mengetahui sistem dan struktur kristal yang terdapat pada material ini dengan menggunakan program GSAS (General Structure Analysis System) dan didapatkan bahwa bahan ini memiliki sistem berupa ortorombik dengan struktur kristal perovskite dan mengenai hasil serapan gelombang elektromagnetik (rentang 9-15GHz) didapatkan hasil serapan paling baik pada bahan dengan variasi Bismuth (Bi) sebesar 0.05 dengan nilai pengukuran reflection loss sebesar -3,881 dB dan didapatkan semakin besar nilai variasi dari Bismuth (Bi) pola serapan dari bahan ini semakin menurun secara perlahan.

The making of La1-xBixMnO3 has been done through mechanical alloying process. It was limited by the variation of doping Bismuth (Bi) which values of 0.05, 0.15, 0.20, 0.25 and 0.35. This material was characterized by using XRD (X-Ray Diffractometer) and VNA (Vector Network Analyzer) to identify what type of system and crystal structure that exist in this material and to obtain the value of its characterization in absorbing electromagnetic waves (range 9-15GHz), respectively.
The result of XRD characterization was processed by using GSAS (General Structure Analysis System) program and the result showed that this materials are orthorhombic with perovskite as their crystal structure and the best result of its absorbing electromagnetic waves (range 9-15GHz) was shown by material which ratio of doping Bismuth (Bi) is 0.05 with reflection loss of -3,881 dB. The pattern of Bismuth (Bi) subtitusion showed that the more ratio of Bismuth (Bi) added, the absorption of this material decreased gradually.

 File Digital: 1

 Metadata

Jenis Koleksi : UI - Skripsi Open
No. Panggil : S43399
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2012
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 47 pages ; illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S43399 14-17-380584900 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20312118
Cover