ABSTRAK
Polymer electrolyte membrane fuel cell (PEMFC) atau yang dikenal juga denganproton exchange membrane fuel cell merupakan salah satu jenis fuel cell yangmemiliki bahan dasar berupa polimer dengan fungsi sebagai alat konversi kimiayang mengubah gas hidrogen dan oksigen menjadi sumber energi listrik, panas,dan air. Salah satu komponen penting dalam PEMFC merupakan pelat bipolar,dimana pelat bipolar tersebut mempunyai fungsi utama untuk mengalirkanelektron dari anoda ke katoda. Bahasan utama dalam penelitian ini adalahmenganalisa pengaruh penambahan fraksi berat multi walled carbon nanotubes(MWCNT) sebesar 1 wt%, 2 wt%, 3wt%, 4 wt%, 5 wt% terhadap karakteristikpelat bipolar PEMFC berbasis nano komposit epoksi. Selain MWCNT, padapenelitian ini juga digunakan grafit limbah Electric Arc Furnace (EAF) sertacarbon black yang dihasilkan dari pirolisis serabut kelapa sebagai penguat. Pelatbipolar dicetak dengan menggunakan metode compression moulding padatemperatur 1000C selama 4 jam. Karakterisasi dalam penelitian ini meliputipengujian densitas, pengujian fleksural, pengujian porositas, pengujiankonduktivitas, serta pengamatan morfologi patahan fleksural denganmenggunakan FESEM. Berdasarkan penelitian ini, didapatkan hasil bahwa pelatbipolar dengan penambahan MWCNT sebesar 5 % mempunyai karakteristik yangoptimum. Dimana nilai densitas adalah ssebesar 1.51 gr/cm3, nilai porositassebesar 1.94 %, nilai fleksural sebesar 63.61 MPa dan nilai konduktivitas sebesar2.30 S/cm. Dari data-data tersebut disimpulkan bahwa penambahan fraksi beratpenguat MWCNT dapat menurunkan porositas dan densitas serta meningkatkannilai konduktivitas listrik dan kekuatan fleksural, dari pelat bipolar PEMFCberbasis karbon polimer komposit.

---

Abstract
Polymer electrolyte membrane fuel cell (PEFMC) or also known as protonechange membrane fuel cell is one type of fuell cell that has the basic materials ofthe polymer material as function of chemical conversion device tha convertshydrogen and oxygen into electrical energy, heat, and water. An importantcomponent of PEMFC is bipolar plate, where in the bipolar plate has a mainfunction to drain electrons from the anode to the cathode. The main discussion ofthis study was to analyze the effect of adding the weight fraction of multi walledcarbon nanotubes (MWCNT) of 1 wt%, 2 wt%, 3 wt%, 4 wt% of thecharacteristic of PEMC bipolar plate based epoksi nano composite. In addition ofMWCNT, in this study also used another reinforcement such as graphit wastefrom electric arc furnace (EAF) and carbon black that made by pyrolisis ofcoconut fiber. Bipolar plates were made by compression moulding method at atemperature of 1000C for 4 hours. Characterization in this study includes densitytesting, porosity testing, fleksural testing, electrical conductivity testing, andobservation of the flexural fracture morphology using FESEM. Based on thisstudy, showed that the addition of 5% weight fraction of MWCNT gives anoptimal characteristic of the bipolar plate, in which the density of the bipolar plateis 1.51 gr/cm3, the value of porosity is 1.94 %, the flexural strength is 63.31 MPa,and the electrical conductivity is 2.30 S/cm. As a conclusion, adding MWCNT asreinforcement in PEMC bipolar plates can reduce density and porosity of. It isalso can improve the electrical conductivity and flexural strength of the PEMFCbipolar plates based on carbon polymer composites.