Synthesis of Na-Y nanozeolite on glassy carbon by seeding method

by Yuni K. Krisnandi, Ivandini T. Anggraningrum, Hany Tovina (Universitas Indonesia, 2011)

 Abstrak

Nanozeolite synthesis was carried out through seeding method, in which the seed was Y zeolite (member of faujasite, FAU, family) using tetraethyl orto silicate (TEOS) as silica source, and aluminium isopropoxide Al[(CH3)2CHO)]3 as aluminum source, and tetramethylammoniumhydroxide (TMAOH) as template, under hydrothermal condition. The seeds then were grown on glassy carbon (GC) sheet, that prior being used was modified, using layer by layer (LbL) technique, with three layers of polyelectrolytes: Poly(diallyldimethylammoniumchloride), PDDA; Poly-4-sodium-styrenesulfonate, PSS; and PDDA again. The seeded GC sheet then was immersed into colloidal suspension with molar composition as follow: 14Na2O: Al2O3: 10SiO2: 798H2O: 3Na2SO4 and the pH of the suspension was kept at 9,0 before was treated hydrothermally for 20 hours at 100oC. The variation on number of seed layers on GC (1, 2 and 3 layers), observed by SEM, showed that homogenous structure and crystal size was obtained with 1 layer of seeds applied on the surface of glassy carbon. When more layers of seeds applied, the agregation and intergrowth of zeolite crystals in the thin film of zeolite became more visible. XRD pattern of the as-prepared thin film zeolite indicates that the zeolite has nanoparticle structure. Furthermore, the pattern of glassy carbon predominated the XRD pattern and covered the pattern of Y-zeolite. On the other hand, XRD of as prepared bulk Y-zeolite shows structure of FAU framework.

 Metadata

Jenis Koleksi : Artikel Jurnal
No. Panggil : J-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Universitas Indonesia, 2011
Sumber Pengatalogan : LibUI eng rda
ISSN : 23391995
Majalah/Jurnal : Makara : Sains
Volume : Vol. 15, No. 1, April 2011: 43-47
Tipe Konten : text
Tipe Media : unmediated
Tipe Carrier : volume
Akses Elektronik : http://journal.ui.ac.id/index.php/science/article/view/876/835
Institusi Pemilik : Universitas Indonesia
Lokasi : Direktorat Riset dan Pengabdian Masyarakat UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
J-Pdf 03-19-263009831 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20326320
Cover