Modifikasi dan karakterisasi bentonit alam Jambi yang diinterkalasi alanin serta aplikasinya sebagai adsorpsi logam cadmium dan timbal = Modification and characterization of Jambi natural bentonite intercalated alanin and its application for cadmium and lead adsorption

Dimas Dwi Saputra; Sihombing, Riwandi, supervisor; Yuni Krisyuningsih, supervisor (Universitas Indonesia, 2013)

 Abstrak

Organoclay dipreparasi dengan cara interkalasi alanin ke dalam antar lapisan fraksi natrium montmorillonit (MMT) dari bentonit Jambi. Interkalasi alanin ke dalam monmorilonit menghasilkan basal spacing lebih besar dari fraksi Na-MMT, meningkat dari 13,28 Å menjadi 17,55 Å dan 19,66 Å. Penentuan KTK menggunakan kompleks tembaga amin, menghasilkan nilai KTK sebesar 42 mek/100 gram Na-MMT. Karakterisasi FTIR Organoclay dinterkalasi alanin sebanyak 1 KTK & 2 KTK, menunjukkan bahwa alanin telah berhasil terinterkalasi ke dalam MMT. Organoclay terinterkalasi alanin diuji daya adsorpsinya terhadap ion logam berat Cd2+ dan Pb2+ dengan variasi waktu, dan konsentrasi, serta membandingkannya dengan daya adsorpsi oleh bentonit alam. Hasilnya menunjukkan bahwa organoclay mengadsorpsi ion Cd2+ lebih besar dibandingkan Pb2+ dan organoclay 2 KTK daya adsorpsinya lebih besar dibandingkan dengan organoclay 1 KTK dan bentonit alam.

The organoclays were modified by intercalating sodium monmorillonite of fraction Jambi natural bentonite with alanine. Intercalation of alanin to the fraction of montmorilonite interlayers resulted an organoclay with a basal spacing greater than fraction of Na-MMT, increased from 13.28 Å to 17.55 Å and 19.66 Å. The CEC of Na-MMT was performed using amine copper complex, and the obtained CEC was 42 mek/100 gram Na-MMT. The FTIR of organoclay intercalated alanine of 1 and 2 CEC showed that alanine has been successfully intercalated into MMT. Organoclay intercalated alanine, as well as raw bentonite, was applied for adsorption of heavy metal cadmium and lead by varying concentration and adsorption time. The results showed that the organoclay have a greater adsorption capacity against Cd2+ rather than Pb2+ and organoclay 2 CEC has a greater adsorption capacity than the 1 CEC organoclay and raw bentonite.

 File Digital: 1

Shelf
 S44168-Modifikasi dan.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S44168
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Universitas Indonesia, 2013
Bahasa : ind
Sumber Pengatalogan :
Tipe Konten :
Tipe Media :
Tipe Carrier :
Deskripsi Fisik : xiii, 45 hlm. : ill. ; 28 cm. + lamp.
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S44168 14-20-608339062 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20331822
Cover