Sintesis tio2 nanotube dengan teknik anodisasi: aplikasi pada sel surya tersensitasi zat warna menggunakan klorofil dan rhodamin b sebagai sensitizer = Synthesis of tio2 nanotube by anodizationtechnique application in dye sensitized solar cell using chlorophyll and rhodamin b as sensitizer

Novi Andini; Faruk, supervisor; Endang Saefudin, examiner; Tresye Utari, examiner; Endang Asijati Widijaningsih Ichsan, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014)

 Abstrak

Fabrikasi Dye-Sensitized Solar Cell (DSSC)menggunakan klorofil dan rhodamin B telah berhasil dilakukan.Bahan semikonduktor sebagai elektroda kerja dalam DSSC yang digunakan adalah TiO2nanotube yang ditumbuhkan pada plat titanium dengan teknik anodisasi, dilanjutkan dengan kalsinasi pada 500⁰C untuk membentuk fasa kristal TiO2. Karakterisasi terhadap Ti/TiO2-NT meliputi Field Emission Scanning Electron Microscope(FE-SEM), UV-VisDiffuse Reflectance Spectrometry (DRS), X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), dan Linear Sweep Voltametry (LSV). Gambar FE-SEM menunjukkan bahwa TiO2 bermorfologi tube dengan diameter 88.99nm. Pola XRD menunjukkan puncak TiO2 anatase pada sudut 2θ: 25, 37,48,54, dan 55 derajat. Karakterisasi UV-Vis menunjukkan nilai bandgap TiO2 sebesar 3.24 eV. Spektrum FTIR menunjukkan keberadaan vibrasi ikatan ~Ti-O-Ti~. Kurva LSV menunjukkan bahwa TiO2 aktif pada daerah UV. Plat Ti/TiO2 dilapisi oleh zat warna melalui teknik elektroforesis dengan variasi waktu 8,10,12, dan 14 menit. Spektrum UV-Vis DRS dari TiO2 yang terlapisi zat warna menghasilkan puncak khas dari masing-masing zat warna, menunjukkan bahwa zat warna telah menempel pada TiO2. Pengujian terhadap performa DSSC menunjukkan nilai efiensi sebesar 0.3565% untuk Ti/TiO2-NT/Klorofil; 0.4351% untuk Ti/TiO2-NT/Rhodamin B; dan 0.3963% untuk Ti/TiO2-NT/Klorofil-Rhodamin B.Indonesia

Fabrication of Dye-Sensitized Solar Cell (DSSC) employing chlorophyll and rhodamine B has been successfully carried out. TiO2 nanotubes which was grown on titanium plate by an anodizationtechniques, followed by calcination at 500⁰C to form a crystalline phase of TiO2, was used as working electrode in the DSSC. Characterization of the Ti/TiO2-NT included Field Emission Scanning Electron Microscope (FE-SEM), UV-Vis Diffuse Reflectance Spectrometry (DRS), X-ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), and Linear Sweep Voltametry (LSV). FE-SEM images showed the tube morphologies of TiO2 with a diameter of 88,99 nm. XRD pattern showed the TiO2 anatase peak at 2θ : 25, 37, 48, 54, dan 55 degree. UV-Vis DRS characterization revealed that the bandgap of the prepared TiO2is 3.24 eV. FTIR spectrum showed the presence of ~Ti?O-Ti~ vibration. LSV curves obtained indicate that the TiO2is active in the UV region . The Ti/TiO2 plate then was being coated with the dye through electrophoresis technique with time variation of 8, 10, 12, and 14 minutes. UV-Vis DRS spectrum of the dyes coated TiO2 showed that all typical dyes realted peaks were observed, indicate that the dyes was attached to the Ti/TiO2-NT. Performance tests of the assembled DSSC showed the efficiencies of 0.3565%for the Ti/TiO2-NT/Chlorophyll; 0.4351% for the Ti/TiO2-NT/Rhodamine B; and 0.3963% for the Ti/TiO2-NT/Chlorophyll/Rhodamine B respectively.

 File Digital: 1

Shelf
 S56100-Novi Andini.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S56100
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; Computer (rdadontent)
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 55 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S56100 14-21-430472696 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20386302
Cover