Fabrikasi dan karakterisasi nano komposit Al-Si-Mg berpenguat Al2O3 dengan variasi fraksi volum 0,5%,1%, 2%,3% dan 5% melalui proses stir casting = Fabrication and characterization of nano composite Al-Si-Mg Al2O3 with variation of 0,5%, 1% ,2%, 3%, and 5 volum fraction produced by stir casting method

Ahmad Hafeizh El Berry; Anne Zulfia, supervisor; Bondan Tiara Sofyan, examiner; Dwi Marta Nurjaya, examiner ([, Fakultas Teknik Universitas Indonesia], 2014)

 Abstrak

[ABSTRAK
Komposit Al-Si-Mg berpenguat partikel Al2O3 berukuran nano memiliki potensi untuk meningkatkan sifat mekanis tanpa mengorbankan keuletan matriks dengan densitas yang rendah. Pada penelitian ini, penambahan fraksi volum Al2O3 sebesar 0.5 %, 1 %, 2 %, 3 %, dan 5 % dilakukan untuk mengetahui titik optimal penambahan partikel Al2O3. Magnesium dengan 3 % fraksi volum digunakan untuk meningkatkan pembasahan antara partikel Al2O3 dan matriks. Fabrikasi dilakukan dengan metode pengecoran aduk karena memiliki nilai ekonomis dibandingkan dengan metode lain. Hasil penelitian menunjukkan penambahan partikel Al2O3 meningkatkan sifat mekanis dari aluminium terutama pada fraksi volum 0.5 %. Kekuatan tarik mencapai 154 MPa dengan elongasi 10.24 %, kekerasan mencapai 37.7 HRB diiringi dengan penurunan laju aus. Tingkat porositas meningkat seiring dengan penambahan fraksi volum yang menjadi penyebab turunnya sifat mekanis dari komposit.

ABSTRACT
, Al-Si-Mg nano composite reinforced with Al2O3 particle have a potential to increase
mechanical properties while maintaining good ductility. In this study, 0.5, 1, 2, 3, and
5 vol. % Al2O3 particle were used in order to know the optimum volume fraction for
high strength composite. Magnesium 3 vol. % were used as wetting agent to increase
wettability between Al2O3 particle and aluminium matrix. Metal matrix nano
composite is produced using vortex/stir casting method. Based on experiment, it was
revealed that the presence of Al2O3 nano particle led to significant improvement in
mechanical properties of aluminium, especially in 0.5 vol. %. The ultimate tensile
strength reach 154 MPa with 10.24 % elongation. Hardness value reach 37.7 HRB
followed by decrement in wear rate. The porosity level tend to increase with
increasing nano Al2O3 volume content and caused decrement in mechanical
properties.]

 File Digital: 1

Shelf
 S56728-Ahmad Hafeizh El Berry.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S56728
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [, Fakultas Teknik Universitas Indonesia], 2014
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 74 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S56728 14-18-452259977 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20387646
Cover