Analisis perbandingan sel surya tersensitasi zat pewarna dari lapisan TiO2 hasil sintesis pasca-hidrotermal dengan TiO2 P-25 degussa = Comparison analysis of dye sensitized solar cell performance made of TiO2 film post hydrothermal synthesis with TiO2 P-25 degussa

Ridwan Sinar Bawono; Bambang Priyono, supervisor; Akhmad Herman Yuwono, examiner; Badrul Munir, examiner (Fakultas Teknik Universitas Indonesia, 2014)

 Abstrak

Performa DSSC terbuat dari nanopartikel TiO2 hasil sintesis Pasca-Hidrotermal dan TiO2 P-25 Degussa dibandingkan melalui tegangan sirkuit terbuka. Perlakuan Pasca-Hidrotermal dilakukan dengan variasi temperatur 100C, 120C, dan 150C selama 14 jam. Pengaruh temperatur pada perlakuan Pasca-Hidrotermal dibandingkan melalui ukuran kristalit, luas permukaan, energi celah pita, dan perbandingan morfologi menggunakan FE SEM.
Hasil karakterisasi serbuk hasil sintesis menunjukkan kecenderungan bahwa pada temperatur 150ºC merupakan titik optimal proses Pasca-Hidrotermal dengan ukuran kristalit 10,55 nm, luas permukaan 95,38 m2/gram, dan energi celah pita 3,16 eV. Sedangkan perbandingan tegangan sirkuit terbuka menunjukkan bahwa sampel Pasca-Hidrotermal 120ºC memiliki nilai paling tinggi sebesar 250 mV.

Performance of DSSC made of TiO2 synthesized by Post-Hydrothermal treatment and TiO2 P-25 Degussa were compared by open circuit voltage. Post-Hydrothermal treatment was treated by various temperature 100C, 120C, and 150C for 14 hours. Effect of temperature in Post-Hydrothermal treatment was investigated by comparison of crystallite size, surface area, band gap energy, and morphology comparison by FE SEM.
Characterization Result of synthesis powder shows indication at temperature 150ºC was optimum process of post-hydrothermal with crystallite size 10.55 nm, surface area 95.38 m2/grams, and band gap energy 3.16 eV. Besides, comparison of open voltage circuit shows Post-Hydrothermal 120ºC sample has highest at 250 mV

 File Digital: 1

Shelf
 S57530-Ridwan Sinar Bawono.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S57530
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2014
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvi, 94 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S57530 14-22-61511975 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20388130
Cover