Dekomposisi selulosa asetat dan selulosa asetat-selulosa asetat butirat dengan penguat organoclay terinterkalasi surfaktan HDTMA-Brr = Decomposition of cellulose acetate and cellulose acetate cellulose acetate butyrate with organoclay intercalated surfactant HDTMA-Br as nanofiller / Ghuzan Al Abrar

Ghuzan Al Abrar; Ariadne Lakshmidevi Juwono, supervisor; Yuni Krisyuningsih, examiner; Cuk Imawan, examiner; Riswijanto, examiner (Universitas Indonesia, 2014)

 Abstrak

ABSTRAK
Sintesis nanokomposit selulosa asetat - selulosa asetat butirat/ organoclay-HDTMA-Br (OCT-C16). Sebagai perbandingan, dalam penelitian ini juga disintesis nanokomposit selulosa asetat. Sintesis organoclay meliputi tiga tahapan yaitu purifikasi karbonat, sintesis Na-Bentonit Purifikasi dan sintesis OCT-C16. Pada tiap tahapan dilakukan karakterisasi dengan XRD, hasil pada sampel organoclay menunjukkan interkalasi pada surfaktan HDTMABr dapat meningkatkan basal spacing organoclay menjadi 19,76 Å. Dilakukan penambahkan variasi persen berat OCT-C16 sebagai nanofiller sebanyak 0 wt%, 1 wt%, 3 wt%, 5 wt%, dan 7 wt% pada nanokomposit selulosa asetat - selulosa asetat butirat. Hasil sintesis dalam bentuk membran di uji tarik, uji dekomposisi dan SEM. Nanokomposit yang dihasilkan mudah terdekomposisi di alam.

ABSTRACT
The formation of nanocomposite cellulose acetate - cellulose acetate butyrate / organoclay ? HDTMA-Br (OCT-C16). As a comparison, in this study also synthesized cellulose acetate nanocomposite. Organoclay synthesis involves three stages , namely purification of carbonate , synthesis of Na - Bentonite Purification and synthesis of OCT-C16 . at each stage were characterized by XRD and the results on samples showed intercalation of organoclay on HDTMABr surfactant can increase the basal spacing of organoclay to 19.76 Å . In the synthesis of nanocomposite cellulose acetate - cellulose acetate butyrate done every additional variation of weight percent OCT-C16 as much as 0 wt% , 1 wt % , 3 wt% , 5 wt% , and wt7 %. Tensile test , decomposition test and SEM to the nanocomposite. The result is biodegradable nanocomposite.

 File Digital: 1

Shelf
 S57761-Ghuzan Al Abrar.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S57761
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Penerbitan : Depok: Universitas Indonesia, 2014
Bahasa : ind
Sumber Pengatalogan : LibUI ita rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 38 pages ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S57761 14-17-180708866 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20402127
Cover