Kekerasan permukaan komposit resin dipolimerisasi dengan Light Curing Unit berbeda iradiansi = Hardness of resin composite polimerized by light curing unit different light irradiance / Sarah Azkianisa

Sarah Azkianisa; Decky Joesiana Indrani, supervisor; Mia Damiyanti, supervisor; Siti Triaminingsih, examiner; Andi Soufyan, examiner (Fakultas Kedokteran Gigi Universitas Indonesia, 2014)

 Abstrak

ABSTRAK
Latar Belakang: LCU prototip dengan metode PWM-kombinasi dengan iradiansi sinar 800, 900, dan 1.000 mW/cm2 telah dibuat untuk mencegah kenaikan suhu pulpa akibat polimerisasi.
Tujuan: Menganalisis kekerasan komposit resin yang dipolimerisasi dengan LCU berbeda iradiansi sinar.
Metode: Spesimen merupakan komposit resin yang dipolimerisasi dengan LCU prototip (PWMkombinasi) beriradiansi sinar 800, 900, atau 1.000 mW/cm2 atau dengan LCU pembanding (900 mW/cm2). Kekerasan komposit resin diukur menggunakan sistem Knoop.
Hasil: Kekerasan komposit resin antar kelompok berbeda bermakna (p<0,05) kecuali yang diberi iradiansi sinar 900 mW/cm2 dari LCU
prototip dan LCU pembanding.
Kesimpulan: Kekerasan komposit resin dipengaruhi oleh iradiansi sinar dari LCU prototip. LCU prototip atau LCU pembanding dengan iradiansi 900 mW/cm2 menghasilkan kekerasan komposit resin yang sama.

ABSTRACT
Background: Prototype light curing unit (LCU) with PWM-combined light
irradiance of 800, 900, and 1.000 mW/cm2 was made to prevent the pulp temperature rise due to the polymerization. Objective: To analyze the hardness of resin composites polymerized by LCU different light irradiation.
Methods: The specimen is resin composites polymerized by prototype LCU light irradiance 800, 900, or 1.000 mW/cm2 or with comparison LCU (900 mW/cm2). Hardness of resin composite test performed by Knoop system.
Result: There is significant differences (p<0.05) among the groups except those between using the prototype LCU and comparison LCU that have irradiance of 900 mW/cm2.
Conclusions: The hardness of resin composite was influenced by the irradiance of prototype LCU. The hardness of resin composite from prototype LCU is equal to those from comparison LCU irradiance of 900 mW/cm2.

 File Digital: 1

Shelf
 S-Sarah Azkianisa.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: Fakultas Kedokteran Gigi Universitas Indonesia, 2014
Bahasa : ind
Sumber Pengatalogan : LibUI ita rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xii, 24 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-Pdf TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20402148
Cover