Sampel nanopartikel coupled magnetite Fe3O4/ZnO dengan tiga variasi rasio molar disintesis dengan metode sol gel. Karakterisasi sampel dilakukan dengan menggunakan Field Emission Scanning Electron Microscope (FESEM), X-ray Diffraction (XRD), Electron Dispersive X-Ray (EDX), spektroskopi UV-Vis dan Vibrating Sample Magnetometer (VSM). Pengujian aktivitas fotokalitik dilakukan dengan mengamati degradasi larutan methylene blue (MB) sebagai model polutan organik di bawah penyinaran cahaya UV. Hasil analisis FESEM menunjukkan sampel nanopartikel coupled memiliki morfologi sferis. Hasil kurva XRD menunjukkan peningkatan intensitas seiring dengan meningkatnya rasio molar ZnO dalam nanopartikel coupled Fe3O4/ZnO. Keberadaan atom Fe, O dan Zn pada sampel nanopartikel coupled dikonfirmasi oleh spektrum EDX. Aktivitas fotokalitik yang paling baik ditunjukkan oleh sampel nanopartikel coupled rasio molar 1:5 dengan dosis sebanyak 20 mg/L pada kondisi pH 13. Nanopartikel Fe3O4 dan nanopartikel coupled Fe3O4/ZnO menunjukkan sifat feromagnetik yang memungkinkan sampel untuk dipisahkan secara magnetik dari dye methylene blue.

---

Nanoparticle coupled magnetite Fe3O4/ZnO with various molar ratio has been syntesized using sol gel method. Characterization using Field Emission Scannig Electron Microscope (FESEM), X-Ray Diffraction (XRD), Electron Dispersive X-ray (EDX), UV-Vis Diffuse Reflectance and Vibrating Sampel Magnetometer (VSM) were conducted to identify morphology, structure, composition, optical and magnetic properties of nanoparticle coupled Fe3O4/ZnO. Photocatalytic activity studied by observing methylene blue (MB) degradation under UV light irradiation. FESEM shows Fe3O4/ZnO has spherical shape. XRD result shows ZnO phase intensity in nanoparticle coupled increase as ZnO molar ratio increase. The peaks corresponding to Fe, O and Zn atom were observed using EDX spectra. Maximum degradation of methylene blue was showed by 20 mg/L nanoparticle coupled with molar ratio 1:5 at pH 13. VSM result shows Fe3O4 and nanoparticle coupled samples exhibit ferromagnetic behavior. Therefore, samples can easily seperate from methylene blue using external magnetic.