Preparasi dan karakterisasi tio2 nanotube dengan metode free standing anodisasi serta pengujian self cleaning pada berbagai bahan = Preparation and characterization of tio2 nanotube with free standing anodization method and self cleaning testing on materials

Annis Safitri Febrianti; Jarnuzi Gunlazuardi, supervisor; Asep Saefumillah, examiner; Helmiyati, examiner; Ismunaryo, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2015)

 Abstrak

Pembuatan TiO2 nanotube telah berhasil dilakukan. TiO2 nanotube dihasilkan dari proses anodisasi plat Ti dalam larutan elektrolit garam flourida dalam etilen glikol. Proses anodisasi dilakukan dengan menggunakan potensial 40 V selama 1 jam. TiO2 nanotube yang terbentuk kemudian didispersikan dalam larutan hidrogen peroksida, sehingga membentuk koloid TiO2. Penggunaan koloid TiO2 salah satunya adalah untuk melapisi TiO2 pada permukaan bahan agar memiliki kemampuan self cleaning.
Pelapisan TiO2 pada kain dan kaca telah berhasil dilakukan. Pelapisan TiO2 pada kain diperlukan penambahan spacer kimia dan perendaman kain dalam koloid TiO2. Pada pelapisan permukaan kaca dengan TiO2 dilakukan dengan cara penetesan koloid TiO2 pada permukaan kaca. Permukaan bahan yang telah dilapisi TiO2 dikarakterisasi dengan menggunakan SEM, UV-Vis DRS, FTIR, dan Contact Angle Meter. Setelah terlapisi dengan TiO2 permukaan kain kaca diuji kemampuan self cleaning dengan menggunakan zat warna Rhodamin B.
Telah didapatkan hasil pengujian aktivitas fotokatalis dari kain dan kaca yang telah terlapisi TiO2 dengan menggunakan iluminasi sinar matahari dan sinar UV. Kain yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 60,67% dengan iluminasi sinar UV selama 100 menit dan sebesar 75,63 % dengan iluminasi sinar matahari selama 180 menit. Kaca yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 53,01% dengan iluminasi sinar UV selama 60 menit, tidak terdeteksi pada 80 dan 100 menit dan sebesar 39,65% dengan iluminasi sinar matahari selama 20 menit, tidak terdeteksi pada 40, 60, 80 dan 100 menit.

Preparation of TiO2 nanotubes have been successfully carried out. The TiO2 nanotubes were produced by anodizing Ti plate in proper electrolyte solution. Anodizing process is performed by using a potential of 40 V for 1 hour. The formed TiO2 nanotubes were then dispersed in the water containing hydrogen peroxide, to obtain TiO2 colloidal. The water base colloidal of TiO2 then was applied to prepare a cloth/fabric and glass those have a self cleaning property. TiO2 coating on the fabric required the addition of a chemical spacer and soaking fabrics in TiO2 suspension.
While surface coating of the glass with TiO2 done by dripping of glass surface in the colloidal of TiO2. The materials those have been coated with TiO2 the were characterized by using SEM, UV-Vis DRS, FTIR, and Contact Angle Meter. In addition the TiO2 coated glass fabric was tested its self-cleaning ability by using Rhodamine B dyes, under illumination of sunlight and UV rays.
The test result of cloth/fabric which has been coated TiO2 showed that under UV light illumination for 100 minutes, it can degrade the dye by 60,67%, while under with sunlight illumination for 180 minutes can degrade up 75,63%. For the glass that has been coated with TiO2, the test showed that, under illumination of UV light for 60 minutes, it can degrade 53,01% of the dye, not detected for 80 and 100 minutes and under illumination of the sunlight for 20 minutes can degrade 39,65% of the dyes, not detected for 40,60,80 and 100 minutes.

 File Digital: 1

Shelf
 S61490-Annis Safitri Febrianti.pdf :: Unduh

LOGIN required

 Kata Kunci

 Metadata

Jenis Koleksi : UI - Skripsi (Membership)
No. Panggil : S61490
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2015
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource (rdacarrier
Deskripsi Fisik : xvi, 72 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S61490 14-22-34472669 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20412949
Cover