Rizqy Pratama Rahman; Nji Raden Poespawati, supervisor; Arief Udhiarto, promotor; Retno Wigajatri Purnamaningsih, examiner (Fakultas Teknik Universitas Indonesia, 2015)

 Abstrak

Skripsi ini bertujuan untuk merancang sel surya dengan menggunakan struktur dasar Triple Junction Solar Cell (TJSC) nc-Si:H/a-Si:H/a-SiGe:H. Lapisan a-SiGe:H pada TJSC tersebut yang merupakan semikonduktor berbahan jenis compound diganti dengan alloy Si1-xGex agar konsentrasi germaniumnya dapat direkayasa untuk mendapatkan sifat lapisan yang lebih baik dan menambah efisiensi sel surya. Setelah itu dilakukan penggantian lapisan a-SiC pada p-layer yang terdapat pada kedua junction tengah dan bawah dengan a-Si dan grading pada lapisan Si1-xGex untuk memperkecil diskontinuitas antara lapisan Si1-xGex dengan lapisan silikon di atasnya dan mengurangi rugi-rugi akibat cacat misfit dislocation. Rancangan disimulasikan dengan menggunakan software wxAMPS dan ditunjukkan hasil akhir sel surya nc-Si:H/a-Si:H/Si1-xGex:H paling optimal yang memiliki efisiensi sebesar 19,081146%, parameter VOC dan ISC sebesar 1,12782 V dan 20,49207 mA, dan parameter fill factor sebesar 82,5620%.

This thesis aims to design a solar cell by using the basic structure of the Triple Junction Solar Cell (TJSC) nc-Si:H/a-Si:H/a-SiGe:H. A layer of a-SiGe:H at the TJSC which is a type of compound semiconductor material is replaced with Si1-xGex alloy so that the germanium concentration can be engineered in order to obtain better layer properties and increase the efficiency of the solar cell. Once that is done then a-SiC on p-layers of the middle and bottom junctions are replaced with a-Si and the Si1-xGex layer is graded to minimize discontinuities between Si1-xGex layer with the layer of silicon on top of it and reduce losses due to the misfit dislocations defects. The design is simulated using wxAMPS software and the results of the final solar cell nc-Si:H/a-Si:H/Si1-xGex:H are shown most optimum which has an efficiency of 19,081146%, VOC and ISC parameters of 1,12782 V and 20,49207 mA, and fill factor parameter of 82,5620%.

 File Digital: 1

Shelf
 S62139-Rizqy Pratama Rahman.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S62139
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: Fakultas Teknik Universitas Indonesia, 2015
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xii, 58 pages : illustration ; 30 cm + Appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S62139 14-17-171092784 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20421410
Cover