Pengaruh doping asam asetat dan fosfat terhadap konduktivitas listrik polianilin pani = Effect of doping acetic and phosphoric acids on electrical conductivity of polyaniline pani

Rustami Shokirzod; Azwar Maas, supervisor ([Publisher not identified] , 2016)

 Abstrak

Polyaniline (PANi) telah sintesis melalui proses polimerisasi melalui penggunaan Ammonium Persulphate (APS) sebagai initiator pada suhu kamar. Selama proses polimerisasi, terjadi peningkatan nilai viskositas cairan polimer dari 436 mPa.s menjadi 1601 mPa.s. Selama proses, juga teramati peningkatan ukuran partikel. Kedua indicator tersebut, terkait dengan terbentuknya rantai molekul polimer ketika berlangsungnya proses polimerisasi. Terbentuknya PANi dapat dipastikan melalui spectrum FTIR sampel hasil sintesis. Hasil penelitian juga menunjukkan, terjadi peningkatan nilai konduktivitas listrik PANi setelah polianilin basa emeraldin (PANi-EB) didop dengan asam lemah. Hasil pengukuran menunjukkan bahwa konduktivitas listrik PANi-EB meningkat dari 50 μS.cm-1 menjadi 1260 μS.cm-1 setelah penambahan asam lemah H3PO4 and 1480 μS.cm-1 setelah penambahan C2H4O2. Disimpulkan bahwa PANi konduktif telah berhasil disintesis melalui proses polimerisasi.

Polyanilines (PANIs) have been synthesized by the polymerization process utilized Ammonium Persulphate as an initiator at room temperature. The complete reaction of polymerization process was indicated by increasing viscosity from 436 mPa.s to 1601 mPa.s. An increase in electrical conductivity of PANi occurred after polyaniline emeraldine base (PANi-EB) doped with weak acids. It is shown that the electrical conductivity of PANi increases from 50 μS.cm-1 to 1260 μS.cm-1 and 1480 μS.cm-1 after doped with weak acids of H3PO4 and C2H4O2 respectively. It is concluded that the conductive PANi has successfully synthesized by the polymerization process.

 File Digital: 1

Shelf
 S62066-Rustami Shokirzod.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S62066
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Bahasa : eng
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvi, 39 pages : illustration ; 28 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S62066 S62066 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20421429
Cover