Studi peningkatan kadar tantalum dan niobium dalam terak timah PT Timah melalui klasifikasi ukuran butir dan pelindian menggunakan larutan naOH dan HCL = Study of upgrading value of tantalum and niobium in PT Timah tin slag by grain size classification and leaching process with naOH and HCL / Ryand Adhyputra

Ryand Adhyputra; Sigit Sapto Wibowo; Sutopo, supervisor; Ahmad Maksum, examiner ([Publisher not identified] , 2015)

 Abstrak

ABSTRAK
Pada penelitian ini akan dilihat pengaruh pemanasan terak timah pada 800℃ yang disertai pendinginan cepat terhadap ukuran butir terak timah, serta variasi waktu pelindian terhadap kadar tantalum dan niobium serta pengotor – pengotornya. Pengujian XRF digunakan untuk melihat perubahan pada terak timah setelah diberi perlakuan pemanasan, pelindian basa dengan NaOH dan pelindian asam dengan HCl. Berdasarkan hasil penelitian didapat bahwa ukuran butir terak timah mengalami reduksi setelah dilakukan pemanasan yang disertai pendinginan cepat. Proses pemanasan, lalu pelindian basa yang diikuti pelindian asam mengakibatkan peningkatan kandungan tantalum dan niobium masing - masing sebesar 374% menjadi 1,564% dan 72% menjadi 1,1%.Waktu optimum untuk pelindian basa adalah 20 menit dan pelindian asam 50 menit.

ABSTRACT
n this research, the heating effect of tin slag at 800℃ followed by rapid cooling and time variation of leaching process to value of tantalum, niobium and its impurities will be observed. XRF test was used to determine the change of tin slag after heating, base leaching and acid leaching process. According to the result, the grain size of tin slag are reduced after the heating process followed by rapid cooling. Heating-rapid cooling process, base leaching and acid leaching have effect on increasing the value of tantalum and niobium in the residue with an enrichment of 374% and 72% respectively. The optimum time of leaching process is 20 minutes for base leaching and 50 minutes for acid leaching.

 File Digital: 1

Shelf
 S61586-Ryand Adhyputra.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S61586
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2015
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 37 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S61586 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20421842
Cover