Studi ketahanan korosi retak tegang Cu-30Zn hasil deformasi plastis canai dingin = Study of stress corrosion cracking cold rolled Cu-30Zn

Nasution, Akhmad Faizal; Rini Riastuti, supervisor; Gadang Priyotomo, supervisor; Dedi Priadi, examiner; Yunita Sadeli, examiner ([Publisher not identified] , 2015)

 Abstrak

Cu-30Zn memiliki ketahanan korosi atmosferik yang baik sehingga banyak digunakan sebagai inti radiator otomotif, komponen amunisi, lamp fixtures, flashlight shells dan kickplates. Cu-30Zn hasil canai dengan deformasi 33,87% pada suhu 300OC dilakukan pengujian SCC. Pengujian Stress Corrosion Cracking (SCC) dilakukan pada larutan Mattson 0,5 M (NH4)2SO4 + 0,05 M CuSO4 dalam kondisi suhu kamar dengan menggunakan beban konstan. Cu-30Zn memiliki kelemahan pada korosi retak tegang pada kondisi lingkungan ammonia. Pengujian SEM menunjukkan Cu-30Zn hasil canai 300oC memiliki arah perambatan transgranular. Selain itu, retak yang terjadi berada pada tegangan dibawah kekuatan luluh dari Cu-30Zn. Hasil EDS menunjukkan adanya indikasi dezincification pada permukaan patahan. Pengamatan visual memperlihatkan adanya perubahan warna dari kuning menjadi merah yang merupakan indikasi dezincification. Cu-30Zn homogen memiliki tingkat ketahanan SCC yang lebih tinggi dari canai dingin Cu-30Zn.

Cu-30Zn has good atmospheric corrosion resistance. Cu-30Zn mainly used as automotive radiator cores, ammunition component, lamp fixture, flashlight shells and kickplates. Cold rolled Cu-30Zn with deformation degree 33,87% at 300OC used in Stress Corrosion Cracking (SCC) test. Stress corrosion cracking (SCC) of a Cu?30Zn has been investigated using Mattsson solutions 0,5 M (NH4)2SO4 + 0,05 M CuSO4 in room temperature by using a constant load method. Cu-30Zn has a weakness on stress corrosion cracking in ammonia environment. SEM testing indicate cold roll Cu-30Zn has transgranular cracking. Furthermore, cracking occur at stress below yield stress. EDS test exhibit dezincification indication on fracture surface. Visual examination show discoloration from yellow to red. Homogenized Cu-30Zn has better SCC resistance than cold rolled Cu-30Zn.

 File Digital: 1

Shelf
 S62011-Akhmad Faizal Nasution.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S62011
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2015
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 60 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S62011 14-17-859849664 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20422434
Cover