Karakterisasi komposit matrik Al-0,12%Zr-0,15%Ce berpenguat Al2O3(np) yang dibuat memalui proses stir casting sebagai bahan alternatif untuk penghantar listrik?.= Characterization of Al-0.2%Zr-0.15%Ce matrix composites reinforced by Al2O3(np) that produced by stir casting process as an alternative material for electrical conductors

Kirman M; Anne Zulfia, promotor; Bambang Suharno, co-promotor; Dedi Priadi, co-promotor; Sutopo, examiner; Winarto, examiner; I Nyoman Jujur, examiner ([Publisher not identified] , 2015)

 Abstrak

ABSTRAK
Paduan AlZrCe dengan komposisi 0.12%wt Zr dan 0,15%wt Cediperkuat dengan partikel nano Al2O3 dari 0.5%Vf hingga 2,0%Vf. Peningkatan keterbasahan partikel Al2O3 pada matrik AlZrCe dilakukan dengan penambahan magnesium. Komposit dikarakterisasi terhadap sifat mekanik, listrik dan termal.Titik optimun dari empat jenis matrik AlZrCe, AlZrCe-2%Mg, AlZrCe-3%Mg, dan AlZrCe-5%Mg terjadi pada rentang 1%Vf hingga 1,2%Vf Al2O3. Kekuatan tarik maksimun 204 MPa terjadi pada 1,2%Vf Al2O3 dengan kadar 5%wt Mg. Efek partikel penguat terhadap penurunan konduktivitas listrik tidak terlalu besar tetapi sebaliknya dengan penambahan 2%wt, 3%wt dan 5%wt Mg menyebabkan penurunan konduktivitas listrik hingga lebih dari 8% IACS yaitu dari 59% IACS untuk komposit tanpa Mg menjadi 52% IACS, 49% IACS dan 45% IACS berturut-turut. Demikian pula sifat ekspansi termal komposit turun dengan penambahan partikel penguat. Penambahan partikel pada aluminium Al2O3 dapat menghaluskan butir sehingga diperoleh ukuran butir yang lebih halus pada fraksi volume 1.0% dan 1,2%. Proses canai dingin dilakukan dengan reduksi 33%, 56% dan 78%yang menghasilkan peningkatan sifat mekanik dan listrik yang maksimumpada pada reduksi 78%.Komposit AlZrCe/1%Vf.Al2O3 reduksi 78% (282MPa, 62,4% IACS) dapat mengungguli kabel konduktor listrik yang telah digunakan dalam transmisi listrik seperti Stabiloy (Al-0.5Fe-0.22Cu) dengan sifat tarik dan listrik yaitu 114MPa dan 61,8% IACS.

ABSTRACT
AlZrCe alloy with a 0.12% wt 0.15 wt% Zr and Ce reinforced with fraction volum of nano particles Al2O3 from 0.5% to 2.0%. Improved wettability of Al2O3 particles in the matrix AlZrCe done with the addition of magnesium. Composites were characterized for mechanical properties, electrical and thermal. Optimum point of the four types of matrices AlZrCe, AlZrCe-2% Mg, AlZrCe-3% Mg, and AlZrCe-5% Mg occurs in the range of 1% to 1.2% VfAl2O3. Maximum tensile strength of 204 MPa occurred in 1.2 %VfAl2O3with levels of 5%wt Mg. Increasing %Vf particle decrease the electrical conductivity is not significant but instead with the addition of 2 wt%, 3 wt% and 5 wt% Mg causes a decrease in electrical conductivity by more than 8% IACS ie from 59% IACS to the composite without Mg to 52% IACS, 49% IACS and 45% IACS respectively. Similarly, the thermal expansion properties of the composite decrease with the addition of reinforced particles. The addition of Al2O3 particles in aluminum can refine the grain in order to obtain a finer grain size on the volume fraction of 1.0% and 1.2%. Cold rolled process carried out by reduction of 33%, 56% and 78%, which results in improved mechanical and electrical properties at the maximum reduction of 78%. Composite AlZrCe/1%Vf.Al2O3with reduction of 78% (282MPa, 62.4% IACS) may exceed the properties of the electrical conductor wires that have been used in power transmission such as Stabiloy (Al-0.5Fe-0.22Cu) whichhas tensile and electricity properties are 114MPa and 61.8% IACS.

 File Digital: 1

Shelf
 D2168-Kirman M.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Disertasi Membership
No. Panggil : D2168
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2015
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 128 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
D2168 10-17-497416201 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20423687
Cover