ABSTRAK
Latar Belakang: MTA bersifat biokompatibel dan dapat digunakan untuk perawatan kaping pulpa. Saat ini dikembangkan semen berbasis kalsium silikat sama seperti MTA dengan penambahan steroid, yaitu Odontocem. Tujuan:Membandingkan efek toksisitas odontocem dan MTA-Angelus terhadap viabilitas sel fibroblas. Metode:Sel fibroblast embrio ayam direndam dalam larutan odontocemdan dan MTA-Angeluspada 24 dan 72 jam. Viabilitas sel dihitung menggunakanMTT Assay. Hasil:Pada kelompok odontcemdan MTA-Angelus, terdapat perbedaan bermakna (p≤0,05 ) dibandingkan dengan kontrol. Pada paparan 24 jam, tidak terdapat perbedaan bermakna antara odontocem dengan MTA-Angelus. Kesimpulan:Odontocem dan dan MTA-Angelus menurunkan viabilitas sel pada 24 jam dan meningkatkan pada 72 jam.ABSTRACT
Background:MTA is proved tobe biocompatible and can be used for pulp capping treatment.Currently, calcium silicate based cement similar to MTA with steroid,called Odontocem has been developed.Objective:To compare effects of odontocem and MTA-Angelus toxicity towards fibroblast cells viability.Method:Fibroblast cells of chicken embryonic were immersed separately in odontocem and MTA-Angelus solution for 24 and 72 hours.Cells viability was analyzed with MTT Assay.Result:There was a significant difference (p>0.05) in Odontocem and MTA-Angelus group compared to control.At the24-hour immersion, there was nosignificant difference between odontocem and MTA-Angelus.Conclusion:Odontocem and MTA-Angelus decreased the viability of fibroblast at 24 hours and increased them at 72 hours.;Background:MTA is proved tobe biocompatible and can be used for pulp capping treatment.Currently, calcium silicate based cement similar to MTA with steroid,called Odontocem has been developed.Objective:To compare effects of odontocem and MTA-Angelus toxicity towards fibroblast cells viability.Method:Fibroblast cells of chicken embryonic were immersed separately in odontocem and MTA-Angelus solution for 24 and 72 hours.Cells viability was analyzed with MTT Assay.Result:There was a significant difference (p>0.05) in Odontocem and MTA-Angelus group compared to control.At the24-hour immersion, there was nosignificant difference between odontocem and MTA-Angelus.Conclusion:Odontocem and MTA-Angelus decreased the viability of fibroblast at 24 hours and increased them at 72 hours.;Background:MTA is proved tobe biocompatible and can be used for pulp capping treatment.Currently, calcium silicate based cement similar to MTA with steroid,called Odontocem has been developed.Objective:To compare effects of odontocem and MTA-Angelus toxicity towards fibroblast cells viability.Method:Fibroblast cells of chicken embryonic were immersed separately in odontocem and MTA-Angelus solution for 24 and 72 hours.Cells viability was analyzed with MTT Assay.Result:There was a significant difference (p>0.05) in Odontocem and MTA-Angelus group compared to control.At the24-hour immersion, there was nosignificant difference between odontocem and MTA-Angelus.Conclusion:Odontocem and MTA-Angelus decreased the viability of fibroblast at 24 hours and increased them at 72 hours.;Background:MTA is proved tobe biocompatible and can be used for pulp capping treatment.Currently, calcium silicate based cement similar to MTA with steroid,called Odontocem has been developed.Objective:To compare effects of odontocem and MTA-Angelus toxicity towards fibroblast cells viability.Method:Fibroblast cells of chicken embryonic were immersed separately in odontocem and MTA-Angelus solution for 24 and 72 hours.Cells viability was analyzed with MTT Assay.Result:There was a significant difference (p>0.05) in Odontocem and MTA-Angelus group compared to control.At the24-hour immersion, there was nosignificant difference between odontocem and MTA-Angelus.Conclusion:Odontocem and MTA-Angelus decreased the viability of fibroblast at 24 hours and increased them at 72 hours.