Rekayasa komposit titania nanotube/karbon aktif/fe3o4 untuk menyisihkan 2,4,6-triklorofenol dalam limbah cair industri pulp dan kertas = Synthesis of magnetically modified composite photocatalyst tio2 nt ac fe3o4 for eliminate 2 4 6 trichlorophenol in wastewaeter of pulp and paper industry

Didik Sudarsono; Slamet, supervisor; Adel Fisli, supervisor; Bambang Heru Susanto, examiner; Setiadi, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Komposit TiO2-NT/karbon aktif/Fe3O4 telah berhasil disintesis dengan menggunakan metode heteroaglomerasi dan digunakan untuk mengeliminasi 2,4,6-Triklorofenol (2,4,6-TCP) dalam limbah cair industri pulp dan kertas. Komposit ini dikarakterisasi dengan menggunakan XRD, FT-IR, SEM-EDX, TEM dan BET. Hasil karakterisasi XRD menunjukkan bahwa komposit TiO2-NT/karbon aktif/Fe3O4 memiliki fasa anatase TiO2 yang dapat mendegradasi polutan dan fasa Fe3O4 yang dapat ditarik oleh medan magnet luar. Hasil karakterisasi FT-IR menunjukkan ikatan elektristatik dari ketiga material yang dikompositkan. Hasil karakterisasi SEM-EDX dan TEM menunjukkan adanya material karbon aktif, TiO2-NT dan Fe3O4 dalam morfologi dan komposisi komposit. Selain itu, hasil karakterisasi BET menunjukkan bahwa komposit mempunyai luas permukaan yang tinggi sebesar 116.8 m2/g. Berdasarkan hasil uji eliminasi 2,4,6-TCP, komposit TiO2-NT/karbon aktif/Fe3O4 memiliki kemampuan menyisihkan 2,4,6-TCP secara efektif. Komposisi komposit dan kondisi operasi optimum yang didapatkan adalah komposisi perbandingan massa TiO2-NT : karbon aktif : Fe3O4 yaitu 1 : 0.02 : 0.1, loading katalis sebesar 1 g/L, penambahan laju alir udara sebesar 500 cc/menit dan konsentrasi awal limbah kurang dari 10 ppm dengan dengan lama irradiasi selama 4 jam. Selain itu, berdasarkan pengukuran waktu separasi komposit menggunakan batang magnet luar, didapatkan bahwa penambahan Fe3O4 dalam komposit mampu mereduksi waktu separasi komposit.

Composite TiO2-NT/activated carbon/Fe3O4 has been successfully synthesized by use heteroaglomeration method and is used to eliminate 2,4,6-trichlorophenol in wastewater of pulp and paper industry. The composite is characterized by using XRD, FT-IR, SEM-EDX, TEM and BET. XRD characterization results indicate composite TiO2-NT/ activated carbon/Fe3O4 has anatase TiO2 to degrade pollutants and Fe3O4 to be pulled by external magnetic field. FTIR characterization results indicate electrostatic bonding of composite materials. SEM-EDX and TEM characterization results indicate the presence of activated carbon material, TiO2-NT and Fe3O4 in morphology and composition. In addition, BET characterization results indicate composite has high surface area of ​​116.8 m2/g. Based on results of elimination of 2,4,6-TCP, TiO2-NT/activated carbon/Fe3O4 have ability to eliminate 2,4,6-TCP effectively. The optimum of composition and operating conditions obtained are composition mass ratio of TiO2-NT : activated carbon : Fe3O4 is 1: 0:02: 0.1, loading the catalyst of 1 g/L, air flow rate of 500 cc/min and an waste initial concentration is less than 10 ppm with irradiation for 4 hours. In addition, based on measurements of time separation composite using an external magnetic rod, it was found that the addition of Fe3O4 in composite is capable of reducing separation time of composite.

 File Digital: 1

Shelf
 S63190-Didik Sudarsono.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S63190
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvi, 103 pages ; illustration ; 22 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S63190 14-18-981985523 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20429559
Cover