Pengaruh penambahan %Vf partikel Nano SiC terhadap sifat mekanik dan mikrostruktur komposit Al6061 produk Stir Casting = Effect of %Vf Nano SiC on mechanical properties and microstructure of Al6061 composite produced by Stir Casting

Karlina Oktaviana Istiqomah; Anne Zulfa, supervisor; Donanta Dhaneswara, examiner; Deni Ferdian, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Penambahan partikel nano SiC kedalam matriks Al6061 menghasilkan material komposit dengan kekuatan mekanis yang tinggi namun tetap mampu mempertahankan sifat ulet. Magnesium sebesar 10% Vf juga ditambahkan sebagai agen pembasah agar didapatkan ikatan yang kuat pada daerah antarmuka. Pada penelitian ini digunakan variasi penambahan partikel nano SiC sebesar 0,05%, 0,10%, 0,15%, 0,20% dan 0,30% untuk mengetahui titik optimal penambahan penguat. Hasil dari penelitian ini menunjukkan penambahan partikel nano SiC optimal di komposisi 0,15%, dengan kekuatan tarik 263,43 MPa, presentase elongasi 7,67%, kekerasan 56,5 HRB, dan harga impak sebesar 0,0550 J/mm2. Peningkatan kekuatan mekanis pada komposit dihasilkan dari kehadiran fasa penguat Mg2Si, distribusi partikel nano SiC yang merata, serta pembasahan yang baik antara matriks dan partikel penguat.

ABSTRACT
The addition of nano SiC particles to Al6061 matrix has enhancing the mechanical properties of metal matrix composite while the ductility properties still maintained. 10% Vf of magnesium were used as wetting agent to achieve strong interface bonding. In the present work, Al6061 reinforced with various amounts (0,05%, 0,10%, 0,15%, 0,20% and 0,30%) of nano SiC were prepared. Results of this study shows the optimum content of nano SiC in Al6061 matrix were 0,15% Vf, with UTS (Ultimate Tensile Strength) reached 263,43 MPa, 7,67% elongation, hardness up to 56,5 HRB, and 0,0550 J/mm2 impact value. The enhancement of mechanical properties of Al6061/SiC composite were influenced by the presence of Mg2Si phase, good distribution of nano SiC particles, and also good interface bonding between matrix and reinforce.
;

 File Digital: 1

Shelf
 S65248-Karlina Oktaviana Istiqomah .pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S65248
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 53 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S65248 14-17-357984904 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20429826
Cover