Modifikasi lensa kontak komersial menggunakan nanopartikel magnetik dan disprosium untuk sistem penghantaran obat = Commercial contact lens modification using magnetite and dysprosium nanoparticles synthesis for drug delivery system

Klanita Sabira; Eny Kusrini, supervisor; Dewi Tristantini Budi, examiner; Elsa Anisa Krisanti, examiner (Fakultas Teknik Universitas Indonesia, 2016)

 Abstrak

Sistem penghantaran obat optalmik dalam bentuk obat tetes mata memiliki waktu tinggal dan bioavailibilitas yang rendah. Maka, untuk meningkatkan waktu tinggal obat pada mata, dilakukan pengujian untuk memuat lensa kontak komersial dengan nanopartikel magnetik (Fe3O4) dan nanopartikel disprosium (Dy). Penelitian dilakukan dengan mensintesis nanosphere Fe3O4-PEG-Dy2O3 dan nanorod Dy(OH)3, kemudian memuat kedua jenis nanopartikel pada permukaan lensa kontak hidrogel poly-2-hydroxyethylmethacrylate (p-HEMA).
Hasil karakterisasi XRD dan TEM menunjukkan nanosphere Fe3O4-PEG-Dy2O3 dan nanorod Dy(OH)3 yang disintesis berukuran ±13,67 nm dan ± 96,50 nm dengan diameter ± 19,30 nm. Kedua jenis nanopartikel yang dihasilkan menunjukkan sifat fotoluminesensi yang sesuai dengan sifat fotoluminensi senyawa disprosium yaitu memiliki emisi warna kuning pada panjang gelombang 575 nm.
Hasil karakterisasi SEM menunjukkan perubahan penampakan permukaan lensa kontak sebelum dan sesudah termuat nanopartikel yaitu dengan penampakan agregat partikel pada permukaan lensa kontak. Efisiensi penempelan dan profil pelepasan nanopartikel pada lensa kontak menunjukan hasil efisiensi muatan terbaik yaitu sebesar 36,12 % oleh nanorod Dy(OH)3 pada konsentrasi 0,50 mg/mL, sedangkan efisiensi muatan terbaik oleh nanosphere Fe3O4-PEG-Dy2O3 adalah sebesar 30,72% pada konsentrasi 0,50 mg/mL. Pelepasan nanopartikel dari permukaan lensa kontak terjadi pada jam ke-6 hingga jam ke-10, yang menunjukan potensi kedua jenis nanopartikel untuk sistem penghantaran obat melalui permukaan lensa kontak.

Ophtalmic drug delivery system via eye drops shows low residence time and low bioavailability. This paper proposes an approach to increase residence time of drug, study conducted of loading magnetic and dysprosium nanoparticles to soft contact lenses for ophthalmic drug delivery. Nanospheres Fe3O4-PEG-Dy2O3 and Dy(OH)3 nanorods have successfully synthesized, then the nanoparticles are loaded to the surface of poly-2-hydroxyethylmethacrylate (p-HEMA) contact lenses.
TEM and XRD characterization results showed that Fe3O4-PEG-Dy2O3 nanospheres and Dy(OH)3 nanorods have sizes of ±13,67 nm dan ± 96,5 nm with diameter ± 19,3 nm respectively. Both nanoparticles showed photoluminescence characteristics of dysprosium which shows emission at 575 nm of yellow luminescent.
SEM image of contact lens showed the difference of blank contact lens and the nanoparticle loaded contact lens with the appereance of particle aggregates on the surface of contact lenses. Nanoparticles attachement efficiency and the nanoparticles release profile were measured shows the best loading efficiency is from Dy(OH)3 nanoparticle with concentration of 0.5 mg/mL, while nanospheres Fe3O4-PEG-Dy2O3 shows 30,72% loading efficiency with concentration of 0.5 mg/mL. Complete nanoparticle release from contact lens happens in 6-10 hours, thus shows the potential of this nanoparticles for drug delivery system via contact lens.

 File Digital: 1

Shelf
 S63690-Klanita Sabira.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S63690
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 61 pages : illustration ; 29 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S63690 14-18-868188447 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20429913
Cover