Studi variasi waktu deposisi pada fabrikasi kaca konduktor fluorine-doped tin oxide fto dengan metode spray pyrolysis = Study of deposition time variations on fabrication of fluorine doped tin oxide fto conductive glass with spray pyrolysis method

Cahya Ahmad Trisdianto; Akhmad Herman Yuwono, examiner; Deni Ferdian, examiner; Badrul Munir, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Kaca konduktor memiliki fungsi strategis di berbagai aplikasi elektronik. Jenis
yang menjanjikan adalah Fluorine-doped Tin Oxide (FTO). Dalam penelitian ini
dilakukan studi pengaruh waktu deposisi (5, 10, 20, 30, dan 40 menit) lapisan tipis
FTO dengan metode spray pyrolysis menggunakan alat ultrasonic nebulizer yang
telah dimodifikasi terhadap nilai karakteristik lapisannya ditinjau dari sifat optis,
kristalinitas, resistivitas, dan mikrostruktur. Variasi juga dilakukan dengan
membandingkan prekursor Sn murni dan larutan yang telah didoping dengan F
sebanyak 2%wt untuk melihat pengaruh penambahan doping F pada larutan
prekursor. Pengujian karakteristik lapisan dilakukan menggunakan XRD, SEM,
UV-Vis spectroscopy, dan digital multimeter. Berdasarkan karakterisasi yang
dilakukan diperoleh nilai terbaik untuk FTO yang dihasilkan adalah pada waktu
deposisi 20 menit dengan nilai transmitansi 74%, energi band gap (Eg) 3,85 eV,
dan sheet resistance (Rs) 7,99 Ω/sq.

ABSTRACT
Conductive glass has strategic functions in various electronic applications. One
of the lead is Fluorine-doped Tin Oxide (FTO). In this research, the effects of
deposition time (5,10,20,30, and 40 minutes) for fabrication of FTO thin film upon
spray pyrolysis process using modified ultrasonic nebulizer on its characteristic
in terms of optical, crystalinity, resistivity and microstructure properties has been
studied. Variation was also performed by comparing the pure Sn precursor and
the solution that has been doped with F 2%wt to see the doping effect to
properties of thin film. The thin film characterization were carried out using XRD,
SEM, UV-Vis spectroscopy, and digital mutlimeter. Based on the results obtained
for the best FTO was generated at the time of deposition is 20 minutes. Providing
74% transmittance, band gap energy (Eg) 3.85 eV and sheet resistance (Rs) 7.99
Ω/sq.

 File Digital: 1

Shelf
 S62876-Cahya Ahmad Trisdianto.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S62876
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 52 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S62876 14-18-742479490 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20430252
Cover