Konversi elektrokimia gas CO2 dan propilen oksida menggunakan katalis deposit Cu = Electrochemical conversion of gas CO2 and propylene oxide using catalyst Cu deposits

Nuryanti Dewi Jayanti; Rahmat Wibowo, supervisor; Widyastuti Samadi, supervisor; Agustino Zulys, examiner; Sunardi, examiner; Yoki Yulizar, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Pemanfaatan penggunaan gas CO2 untuk dikonversi menjadi senyawa yang memiliki nilai tambah semakin meningkat karena meningkatnya perhatian terhadap pemanasan global. Reduksi CO2 secara elektrokatalik untuk membentuk senyawa siklik karbonat dengan adanya epoksida merupakan topik yang cukup menarik. Pada penelitian ini dilakukan elektrosintesis senyawa kimia dari reduksi CO2 dan propilen oksida menggunakan katalis Cu. katalis Cu disintesis pada permukaan elektroda emas dengan metode elektrodeposisi pada potensial -3,1 V vs Ag/AgCl selama 5 menit. Deposit yang terbentuk dikarakterisasi menggunakan SEM-EDS. Deposit yang terbentuk berbentuk foam dengan adanya penambahan bahan aditif PEG (Polietilen Glikol). Hasil Deposit yang terbentuk digunakan sebagai katalis untuk mereduksi CO2 dan dipelajari dengan metode siklik voltametri dengan cairan ionik [BMIM][PF6] dalam asetonitril. Reduksi CO2 teramati pada potensial -1,9 V vs Ag/AgCl dan diaplikasikan untuk membentuk senyawa kimia dari CO2 dan propilen oksida . Proses sintesis dilakukan pada sel yang tidak terpisah dan dilakukan pada suhu ruang. Produk yang dihasilkan dikarakterisasi menggunkan Fourier Transform Infra Red (FTIR) dan Gas Chromatography-Mass Spectrometer (GC-MS). Dari hasil karakterisasi produk yang terbentuk adalah tripropilen glikol, 1-propil-1-sikloheksen, sikloheksanol dan 4-propil-sikloheksanol.

ABSTRAK
The use of CO2 for converted into value added compounds has dramatically increased due to increased global warming concerns. Reduction of CO2 to form cyclic carbonate compound with the epoxide is interesting topic. In this research chemical compounds will be synthesized from the reduction of CO2 and propylene oxide using Cu deposit catalyst. Cu catalysts synthesized on the surface of a gold electrode by electrodeposition method at potential -3.1 V vs Ag / AgCl for 5 minutes. Deposits formed were characterized using SEM-EDS. Deposits are shaped foam with the addition of additives PEG (Polyethylene Glycol). Deposits were used as a catalyst to reduce CO2 and studied by cyclic voltammetry method with ionic liquids [BMIM][PF6] in acetonitrile. CO2 reduction potential was observed at -1.9 V vs Ag/AgCl and applied to synthesize chemical compounds from CO2 and propylene oxide. The synthesis process using undivided cell and performed at room temperature. The resulting products were characterized using the Fourier Transform Infra Red (FTIR) and Gas Chromatography-Mass Spectrometer (GC-MS). The products are tripropylene glycol, 1-propyl-1-cyclohexene, 4-propyl-cyclohexanol.

 File Digital: 1

Shelf
 S64954-Nuryanti Dewi Jayanti.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S64954
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 58 pages : illustration ; 29 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S64954 14-18-900656289 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20432115
Cover