Modifikasi intermetallic katalis nikel untuk menurunkan kekuatan asam dalam hidrogenasi karbon monoksida dan karbon dioksida menjadi metanol = Modification intermetallic nickel catalyst to reduce acid strength in hydrogenation of carbon monoxide and carbon dioxide to produce methanol

Astri Pertiwi; Mohammad Nasikin, supervisor; Adiarso, supervisor; Sukirno, examiner; Setiadi, examiner; Yuliusman, examiner (Fakultas Teknik Universitas Indonesia, 2016)

 Abstrak

Modifikasi dilakukan pada sistem katalis yang terdiri dari logam Ni dan Zn sebagai promotor dengan penyangga karbon aktif agar dapat menurunkan keasaman dalam menghidrogenasi CO dan CO2 secara simultan menjadi metanol. Karbon aktif berasal dari batubara bituminous yang mengandung unsur Si, Al, Fe, Ca, S dan Mg. Katalis dibuat secara impregnasi dilanjutkan dengan pengeringan dalam oven 110oC selama 20 jam dan kalsinasi pada suhu 400oC selama 4 jam. Tahap awal uji aktivitas katalis didahului oleh reduksi secara in-situ dalam fixed bed reactor dengan massa katalis 0.5 gram selama 1.5 jam pada suhu 350oC menggunakan gas H2 sebagai pereduksi. Proses hidrogenasi CO dan CO2 dilangsungkan pada kondisi 20 bar dan suhu 270oC selama 4 jam kontinyu. Sebagai umpan digunakan campuran gas H2/CO/CO2/N2 dengan komposisi 69.98% H2, 17.78% CO, 6.41% CO2, 5.75% N2 dan 0.08% CH4. Katalis dengan loading Ni tertinggi (57.58% Ni dan 9.46% Zn) dengan keasaman 0.1565 mmol/g.Kat dan luas area permukaan 758.04 m2/gram menghasilkan konversi CO2 tertinggi sebesar 97.72% dan konversi CO sebesar 12.34% untuk membentuk CH4, C2H4, C2H6 dan metanol.

Modifications carried out on a catalyst system consisting of Ni metal and Zn as a promoter with activated carbon as a support in order to lower the acidity in the hydrogenate of CO and CO2 that simultaneously produce methanol. Activated carbon derived from bituminous coal containing elements of Si, Al, Fe, Ca, S and Mg. The catalyst is made by impregnation followed by drying in an oven 110oC for 20 hours and calcination at a temperature of 400oC for 4 hours. The initial stage of the catalyst activity test was preceded by in-situ reduction in the fixed bed reactor with a catalyst mass of 0.5 grams for 1.5 hours at a temperature of 350oC using H2 as a reductant. The process of hydrogenation of CO and CO2 held in conditions of 20 bar and a temperature of 270oC for 4 hours continuously. gas mixture (H2 / CO / CO2 / N2) is used as a feedstock with each composition 69.98% H2, 17.78% CO, 6:41% CO2, 5.75% N2 and 0.08% CH4. Nickel catalyst with the highest loading (57.58% 9:46% Ni and Zn) with the acidity 0.1565 mmol /g.Kat and surface area 758.04 m2/gram have the highest conversion of CO2 97.72% and the conversion of CO reach 12.34% to form CH4, C2H4, C2H6 and methanol.

 File Digital: 1

Shelf
 T45691-Astri Pertiwi.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T45691
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvi, 108 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T45691 15-17-627434856 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20432547
Cover