Peningkatan kadar SnO2 dari mineral kasiterit melalui proses dekomposisi basa natrium karbonat (Na2CO3) = Extraction SnO2 of mineral cassiterite by the alkaline decomposition process with natrium carbonate (Sa2CO3) / Lia Andriyah

Lia Andriyah; Azwar Maas, supervisor; Latifa Hanum, supervisor; Nurlely, examiner; Rudi Subagja, examiner; Iskandar Muda, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Ekstraksi kasiterit dari Indonesia menggunakan dekomposisi basa telah
dilakukan. Dekomposisi basa yang digunakan pada penelitian ini adalah natrium karbonat (Na2CO3). Kasiterit merupakan mineral oksida dari timah (SnO2) yang mempunyai komposisi berkisar 73,4% dan masih mengandung banyak pengotor seperti kwarsa, ilmenit, monazit, rutil dan zirkon. Proses pendahuluan untuk menghilangkan pengotor pada kasiterit adalah pencucian dan pemisahan high magnetic separator (HTS). Percobaan ini bertujuan untuk meningkatkan nilai tambah kasiterit dari lokal area Indonesia yang menggunakan dekomposisi basa untuk membentuk natrium stannat (Na2SnO3). Hasil percobaan menunjukkan bahwa kasiterit dari Indonesia dapat membentuk natrium stannat (Na2SnO3) yang dapat larut dengan air pada proses leaching. Semakin lama waktu dekomposisi menyebabkan fasa natrium stannat yang terbentuk makin banyak. Hasil optimum dicapai ketika proses dekomposisi dilakukan pada suhu 870 oC selama 4 jam dengan persentase produk mencapai 61%. High score plus (HSP) digunakan dalam penelitian ini untuk menganalisa berat natrium stanat dan SnO2. Analisa HSP menunjukkan bahwa berat fasa natrium stannat (Na2SnO3) yang terbentuk > 70 wt % dan produk akhir SnO2 sebesar 100 wt %.

ABSTRACT
Extraction of cassiterite from Indonesia using alkaline decomposition has
done. The alkaline decomposition that used in this research is natrium carbonate (Na2CO3). Cassiterite is a mineral oxide from tin (SnO2) that has a composition about 73.4% and many impurities such as quartz, ilmenite, monazite, rutile and zircon. Preliminary processes to remove the impurities in cassiterite are washing and separation of high magnetic separator (HTS). Aim of this research is to increase the added value of cassiterite from local area Indonesia that using alkaline decomposition to form natrium stannate (Na2SnO3). The result shows that cassiterite from Indonesia can form natrium stannate (Na2SnO3) which soluble with water in leaching process. The longer the time for decomposition, the more phases of natrium stannate that will be formed. Optimum result reached when the decomposition process was done in 870 ÂșC for 4 hours with the percentage of yield is 61%. High Score Plus (HSP) was used in this research to analyze the mass of natrium stannate (Na2SnO3) and SnO2. HSP analysis showed that mass of natrium stannate (Na2SnO3) is more than 70 wt% and mass of SnO2 product is 100 wt%.

 File Digital: 1

Shelf
 T46459-Lia Andriyah.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T46459
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvii, 98 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T46459 15-18-959430610 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20433385
Cover