Elektroreduksi karbon dioksida (CO2) menjadi fine chemicals dengan elektroda boron-doped diamond (BDD) yang termodifikasi IrO2 = Electroreduction of carbon dioxide (CO2) into fine chemicals using boron doped diamond (BDD) modified by IrO2 / Andi Muhammad Ichzan

Andi Muhammad Ichzan; Sultan Badjri, supervisor; Jarnuzi Gunlazuardi, supervisor; Asep Saefumilah, examiner; Yoki Yulizar, examiner; Rahmat Wibowo, examiner; Widayanti Wibowo, examiner ([Publisher not identified] , 2017)

 Abstrak

ABSTRAK
Boron-doped diamond BDD dimodifikasi dengan iridium dioksida IrO2 untuk aplikasi dalam reaksi reduksi CO2. Deposisi IrO2 pada permukaan BDD dilakukan menggunakan teknik kronoamperometri pada potensial 1,2V menggunakan larutan pendeposit yang terdiri dari larutan garam iridium 0,5 mM dan KNO3 0,1 M 1:1 . Hasil karakterisasi dengan XPS memperlihatkan bahwa spesies iridium yang terdeposit pada permukaan BDD adalah IrO2 dengan energi ikat sebesar 62,8 eV. Modifikasi permukaan elektroda BDD dengan IrO2, memperlihatkan peningkatan performa elektroda yang terlihat dari dihasilkannya produk elektroreduksi CO2 berupa asam format, asam asetat, karbon monoksida dan hydrogen dengan total efisiensi penggunaan arus sebesar 71,03 . Efisiensi arus yang digunakan untuk menghasilkan asam asetat sebesar 26,62 dengan rata-rata konsentrasi sebesar 2,22mg/L ,menjadikan asam asetat sebagai produk utama dari elektroda BDD termodifikasi IrO2. Sementara itu elektroda glassy carbon termodifikasi IrO2 menghasilkan produk elektroreduksi CO2 berupa formaldehida, gas karbon monoksida, gas metana, dan gas hidrogen dengan total efisiensi faraday sebesar 41,23 dengan gas karbon monoksida sebagai produk utama. Kata Kunci:IrO2, Elektroreduksi CO2, Boron-Doped Diamond, Asam asetat

ABSTRACT
Boron doped diamond BDD has been modified with iridium dioxide IrO2 for an application in CO2 reduction. IrO2was deposited atthe surface of BDD using chronoamperometric technique at anapplied potential of 1.2V. A solution consisting of iridium salt solution 0.5 mM and nbsp KNO3 0.1 M 1 1 was used. Characterization by XPS showed that iridium species deposited on the surface of BDD was IrO2with a binding energyof 62.8 eV . The modified BDD with IrO2 showed an increase of electrode performance in CO2 electroreduction with the productsof formic acid, acetic acid, carbon monoxide, and hydrogen with a total faradaic efficiency of71.03 . The faradaic efficiency used to produce acetic acid was 26.62 with an average concentration 2.22mg L,makesthe acetic acid as the main product of IrO2 modified BDD electrode. Meanwhile, IrO2 modified glassy carbon produced formaldehyde, carbon monoxide, methane, and hydrogen as the carbon dioxide electroreduction products with total faradaic efficiency 41,23 and carbon monoxide as the major product. nbsp nbsp nbsp Keywords IrO2, Electroreduction of CO2, Boron Doped Diamond, Acetic acid nbsp

 File Digital: 1

Shelf
 T47089-Andi Muhammad Ichzan.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T47089
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2017
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 110 pages: illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T47089 15-19-454516415 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20446664
Cover