Organic photovoltaic (OPV) devices have lower efficiency, shorter lifetimes, faster degradation, and poorer stability than
inorganic photovoltaics (IPV) in ambient conditions. In this paper, the equivalent electrical circuit of a two-diode model
effectively extracts the model-fit electrical photovoltaic (PV) parameters from degraded OPV devices, especially the
series (Rs) and shunt (Rsh) resistances. The result shows a better correlation between the resistances of the devices and
performance of the devices over the degradation process where the devices are deliberately exposed to ambient conditions
under constant illumination. The degradation of the devices is mostly caused by the degradation of the aluminum (Al)
electrode from water and oxygen, which correlates to the Rs. However, it is possible that the degradation of the bulk active
layer can also occur due to the constant illumination on the device, which causes a reduction of photocurrent.
Aplikasi Model Rangkaian Setara untuk Memantau Degradasi Sel Fotovoltaik Organik. Divais fotovoltaik organik
(OPV) memiliki efisiensi yang lebih rendah, masa hidup lebih pendek, degradasi lebih cepat, dan stabilitas lebih rendah
dari photovoltaics anorganik (IPV) pada kondisi udara terbuka. Pada tulisan ini, rangkaian setara dari model dua-dioda
secara efektif mengekstrak parameter-parameter listrik fotovoltaik (PV) dari divais OPV yang terdegradasi, khususnya
resistansi seri (Rs) dan resistansi paralel (Rsh). Hasilnya menunjukkan suatu korelasi yang lebih baik antara resistansi
divais dan kinerja divais selama proses degradasi dimana divais diberi pencahayaan konstan pada kondisi udara terbuka.
Degradasi divais ini sebagian besar disebabkan oleh degradasi elektroda aluminium (Al) yakni oleh air dan oksigen, yang
berkorelasi dengan Rs. Namun, ada kemungkinan bahwa degradasi lapisan aktif juga dapat terjadi karena pencahayaan
konstan pada divais, yang menyebabkan pengurangan photocurrent.