Pengaruh Material Karbon dan Metal Oksida TiO2 terhadap Aktivitas Katalitik Perovkite LaFeO3 = The Influence of Carbon Materials and Titanium Dioxide on Catalytic Performance of Perovskite LaFeO3.

Nur Afifah; Rosari Saleh, supervisor; Djoko Triyono, examiner; Dede Djuhana, examiner; Efta Yudiarsah, examiner ([Publisher not identified] , 2017)

 Abstrak

ABSTRAK
Aktivitas katalitik perovskite LaFeO3 diuji dengan menggunakan zat pewarna methylene blue sebagai model polutan organik. Material karbon dan oksida besi TiO2 ditambahkan untuk meningkatkan aktivitas katalitik perovskite tersebut. Katalis yang akan digunakan disintesis dengan menggunakan metode ko-presipitasi dan sol-gel. Sampel yang telah disintesis kemudian di karakterisasi dengan menggunakan spektroskopi X-ray diffraction XRD, Thermogravimetric Analysis TGA, Energy Dispersive X-Ray EDX, UV-Visible Diffuse Reflectance Spectroscopy UV-Vis DRS, Vibrating Sample Magnetometer VSM, and Brunauer-Emmett-Teller BET. Hasil yang diperoleh menunjukkan bahwa penambahan material karbon dan TiO2 dapat meningkatkan aktivitas katalitik perovskite LaFeO3. Tergabungnya material karbon dan TiO2 dapat meghambat laju rekombinasi elektron dan hole dengan tersedianya electron transport layers dan junction level pada masing-masing sampel sehingga aktivitas katalitik yang diperoleh juga semakin meningkat.

ABSTRACT
The catalytic performance of perovskite LaFeO3 was tested using methylene blue as a model of organic pollutant. Carbon materials and titanium dioxide were added to improve its catalytic performance. The prepared catalyst was synthesized using co precipitation and sol gel method. The samples were characterized using X ray diffraction XRD, Thermogravimetric Analysis TGA, Energy Dispersive X Ray EDX, UV Visible Diffuse Reflectance Spectroscopy UV Vis DRS, Vibrating Sample Magnetometer VSM, and Brunauer Emmett Teller BET surface area analysis. The results showed that the catalytic performance increased with the incorporation of carbon materials and TiO2 on the samples. The role of carbon materials and TiO2 incorporation could provide the junction level and electron transport layers, respectively, thus could inhibit the recombination of electron and hole rate and improve the catalytic performance.

 File Digital: 1

Shelf
 T48186-Nur Afifah.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T48186
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2017
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated
Tipe Carrier : volume
Deskripsi Fisik : xi, 47 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T48186 136-17-201168679 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20455091
Cover