Studi awal impregnasi perak oksida terhadap zeolit alam Lampung sebagai adsorben untuk pengayaan oksigen dari udara dengan teknik PSA = Preliminary design of silver oxide impregnated Lampung natural zeolite as an adsorbent to produce oxygen enriched air using PSA technique

Adenia Gita Dianty; Setijo Bismo, supervisor; Eva Fathul Karamah, examiner; Nelson Saksono, examiner ([Publisher not identified] , 2017)

 Abstrak

Oksigen dengan kemurnian yang tinggi dapat dimanfaatkan untuk berbagai hal. Metode pemurnian oksigen yang akan diaplikasikan pada penelitian ini adalah teknik Pressure Swing Adsorption PSA . Adsorben yang akan digunakan adalah zeolit alam, yaitu ZAL Zeolit Alam Lampung . Zeolit alam memiliki sifat non-polar, sehingga akan mengadsorpsi gas dengan momen quadrupol tinggi, yaitu nitrogen. Variabel bebas pada penelitian ini adalah ukuran adsorben dan konsentrasi aktivator asam H2SO4. Ukuran adsorben yang digunakan adalah 18-35 mesh, 35-60 mesh, dan 60-100 mesh. Konsentrasi aktivator asam H2SO4 yang digunakan adalah 1M, 2M dan 3M. Adsorben diaktivasi dengan aquademin, H2SO4, NaOH, dan kalsinasi. Selain itu, akan dilakukan modifikasi pada ZAL dengan teknik impregnasi basah menggunakan larutan AgNO3, dengan -loading nominal 1 -berat. Adsorben dikarakterisasi menggunakan BET, FTIR, XRF, XRD dan SEM-EDX Adsorben 35-60 mesh 1M menunjukkan hasil adsorpsi terhadap molekul nitrogen yang paling tinggi, dengan peak terendah sebesar 60356 V. Didapatkan juga bahwa ZAL-lah yang memiliki peran utama dan dominan dalam mengadsorpsi nitrogen, sementara AgxO tidak memberikan pengaruh yang signifikan pada kinerja adsorben.

High purity oxygen can be used for various things. Oxygen purification method to be applied on this research is the Pressure Swing Adsorption PSA technique. The adsorbent that would be used is a natural zeolite, namely ZAL Zeolit Alam Lampung . Natural zeolite has non polar properties, so it will adsorb gas with high quadrupole moment, which is nitrogen. The varied variable is the size of adsorbent and the concentration of H2SO4. The sizes are 18 35 mesh, 35 60 mesh, and 60 100 mesh. While the H2SO4 concentration are 1M, 2M and 3M. The The adsorbent will be activated in aquademine, H2SO4, NaOH, and through a calcination process. Moreover, ZAL will also be modified by wet impregnation technique using AgNO3 solution with 1 wt loading nominal. The adsorbents were characterized using BET, FTIR, XRF, XRD and SEM EDX. ZAL 35 60 mesh 1M showed the best performance on adsorbing nitrogen, with its lowest peak at 60356 V. The result of this research suggested that ZAL itself has the main role on adsorbing nitrogen, while AgxO did not give any significant effect.

 File Digital: 1

Shelf
 S67680-Adenia gita dianty .pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S67680
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2017
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 111 pages : illustration ; 29 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S67680 14-19-115797408 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20456402
Cover