Pengaruh diameter pin dan dwell time tahap kedua terhadap kekuatan geser pada pelat tipis alumunium aa 1100 dengan pengelasan two-stage refilled micro friction stir spot welding (TFSSW) = Effect of tool diameter and second stage dwell time to shear strength on two-stage refilled friction stir spot welding (TFSSW) of thin plate alumunium aa 1100

Muhammad Andre Widianto; Ario Sunar Baskoro, supervisor; Henky Suskito Nugroho, examiner; Saragih, Agung Shamsuddin, examiner ([Publisher not identified] , 2017)

 Abstrak

ABSTRAK
Teknologi pengelasan friction stir spot welding FSSW merupakan pengelasan pada solid state welding sehingga dapat mengatasi kerusakan, karena tidak memerlukan temperatur yang tinggi. Two-stage refilled friction stir spot welding TFSSW merupakan pengelasan tahap kedua untuk pengisian lubang yang terbentuk pada pengelasan FSSW. Penelitian ini mencari pengaruh besar diameter pin dan dwell time tahap kedua terhadap kekuatan geser pengelasan. Material yang digunakan yaitu Alumunium Al 1100 dengan ketebalan 0,4 mm dan kecepatan spindle 33.000 rpm. Parameter yang digunakan pada penelitian ini yaitu variasi diameter pin 2 mm, 2.5 mm, dan 3 mm dan variasi dwell time tahap kedua 4 detik, 6 detik, dan 8 detik . Analisis makro dilakukan terhadap hasil pengelasan di setiap variabel.

ABSTRACT
Friction stir spot welding technology is a solid state welding that can overcome damages caused by high temperatures. Two stage refilled friction stir spot welding TFSSW is a second step to refill keyhole that formed after conventional FSSW process. This study is to analyze the effect of tool diameter and second stage dwell time on TFSSW to the shear strength of welds. Alumunium material Al 1100 with thickness 0,4 mm was used and spindle speed was at 33.000 rpm. Parameters used in this study were the variable of tool diameter 2 mm, 2.5 mm, and 3 mm and variable of second stage dwell time 4 seconds, 6 seconds, and 8 seconds . Analysis of macro structure was studied on variation of welds.

 File Digital: 1

Shelf
 S67798-Muhammad Andre Widianto.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S67798
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2017
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xviii, 47 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S67798 14-19-882904655 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20456861
Cover