Karakterisasi komposit aluminium ADC12 berpenguat nano siC dengan variasi penambahan penghalus butir titanium boron melalui metode pengecoran aduk = Characterization of ADC12/nano siC composite with variation of TiB as grain refiner through stir casting method

Theodora Pradnya Pramudita; Anne Zulfia, supervisor; Donanta Dhaneswara, examiner; Deni Ferdian, examiner; Budi Wahyu Utomo, examiner ([Publisher not identified] , 2017)

 Abstrak

ABSTRAK
Penambahan partikel penghalus butir Ti-B dalam matriks ADC12 berpenguat nano SiC mampu meningkatkan sifat mekanis komposit dengan mekanisme penghalusan butir. Ti-B ditambahkan dengan tujuan menghasilkan Al3Ti sebagai nuklean dan memodifikasi struktur dendritik menjadi globular. Penambahan magnesium sebesar 10 bertujuan sebagai agen pembasah agar didapatkan ikatan antarfasa antara matriks dan penguat partikel nano SiC. Pada penelitian ini ditambahkan 0.15 Vf nano SiC dan variasi penambahan Ti-B 0.0 , 0.02 , 0.04 , 0.06 , dan 0.08 wt . Hasil penelitian dikarakterisasi secara komposisi dengan OES dan XRD, mikrostruktur dengan OM dan SEM, kemudian diuji mekanis tarik, keras, aus, dan impak. Komposisi paling optimal yaitu pada penambahan 0.04 wt TiB, yang menghasilkan nilai kekuatan tarik 135.9 MPa, kekerasan 45.6 HRB, laju aus 1.47x10-5 mm3/s, dan harga impak 0.0225 J/mm2. Peningkatan penambahan Ti-B linear dengan reduksi ukuran butir, namun penambahan lebih dari 0,04 wt tidak menunjukkan perubahan ukuran butir secara signifikan. Selain karena penghalusan butir akibat Al3Ti, peningkatan kekuatan mekanis terjadi akibat terbentuknya fasa MgAl2O4 pada antarmuka partikel nano SiC dan matriks ADC12.

ABSTRACT
Addition of Ti B grain refiner in ADC12 nano SiC composite results in improvement of mechanical properties through grain refinement mechanism. Ti B was added to form Al3Ti as nucleant and modify the dendritic structure into globular. 10 of Mg added as a wetting agent to improve wettability between nano SiC as reinforce and ADC12 as matrix to maintain a good interphase. In this study, used 0.15 vf of nano SiC and few variations of TiB respectively 0.0 , 0.02 , 0.04 , 0.06 , dan 0.08 wt . Several test were conducted to characterize the material OES, XRD, OM, SEM, and destructive test tensile, hardness, wear, and impact . Obtained the best composition is 0.04 wt TiB which results 135,9 MPa in Ultimate Tensile Strength UTS , 45.6 HRB in hardness, 1.47x10 5 mm3 s as wear rate, impact strength 0.0225 J mm2. The increase of Ti B addition results in grain refinement but the addition more than 0,04 wt gives no significant results. The increase in mechanical properties of composites mainly because of Al3Ti acts as nucleant which initiates the grain refinement and the existence of MgAl2O4 phase which indicates a good interphase between nano SiC and ADC12 matrix.

 File Digital: 1

Shelf
 S68554-Theodora pradnya pramudita .pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S68554
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2017
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 60 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S68554 14-19-531537092 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20457172
Cover