Pengaruh konsentrasi natrium klorida terhadap ketahanan korosi pada baja tahan karat duplex dan feritik menggunakan metode electrochemical impedance spectroscopy = The use of electrochemical impedance spectroscopy method for corrosion resistance evaluation of duplex and ferritic stainless steels in aqueous sodium chloride solutions

Sirait, Geraldo Joseph Frideandra; Yunita Sadeli, supervisor; Rini Riastuti, examiner; Yudha Pratesa, examiner (Fakultas Teknik Universitas Indonesia, 2017)

 Abstrak

Perilaku korosi dari baja tahan karat duplex 2205 dan feritik 410s diamati dalam berbagai konsentrasi larutan sodium klorida. Rangkaian pengujian dilakukan dengan menggunakan metode Electrochemical Impedance Spectroscopy pada suhu ruang. Metode ini dilakukan untuk mengamati impedansi dari material uji. Konsentrasi larutan klorida disiapkan dengan variasi 1, 2, 3, 4 dan 5 w.t. Hasil pengujian terhadap kedua sampel menyatakan bahwa sistem dengan ketahanan korosi paling rendah adalah sistem yang menggunakan 3,5 w.t sodium klorida, yang serupa dengan kandungan klorida air laut. Hasil pengujian juga menyatakan bahwa baja tahan karat duplex 2205 secara umum lebih tahan korosi dibandingkan dengan feritik 410s pada setiap konsentrasi klorida.

Corrosion behaviour of SS 2205 and SS 410s were investigated in various concentrations of aqueous sodium chloride solutions. Experimental work was carried out by using electrochemical impedance spectroscopy method at room temperature to evaluate the impedance of the system. Sodium chloride solutions were prepared with various concentration i.e. 1, 2, 3.5, 4 and 5 w.t. The testing results were represented by Nyquist plot for both alloys. It was observed that the lowest corrosion resistance of both alloys was at 3,5 w.t NaCl which was similar to typical seawater solution. It was also observed that SS 2205 had better corrosion resistance along with greater impedance than the SS 410s in every NaCl concentration.

 File Digital: 1

Shelf
 Sirait, Geraldo Joseph Frideandra.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2017
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online
Deskripsi Fisik : xiv, 49 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-Pdf 14-21-684658594 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20465906
Cover