Sintesis ZnO-NP, WO3-NP, dan nanomaterial ZnO-WO3 dilakukan menggunakan ekstrak daun tembakau sebagai sumber basa lemah dan capping agent. Nanopartikel dan nanomaterial hasil sintesis dikarakterisasi menggunakan FTIR, UV-Vis DRS, dan XRD. Hasil karakterisasi dengan FTIR menunjukkan adanya ikatan Zn-O dan W-O pada nanomaterial ZnO-WO3. Hasil karakterisasi UV-Vis DRS menunjukkan bahwa ZnO-NP memiliki band gap 3.21 eV, WO3-NP memiliki band gap 2.30 eV, dan nanomaterial ZnO-WO3 memiliki band gap 2.60 eV. Hasil karakterisasi XRD menunjukkan bahwa ZnO-NP memiliki struktur kristal heksagonal, WO3-NP memiliki struktur kristal triklinik, dan nanomaterial ZnO-WO3 memiliki peak gabungan ZnO-NP dan WO3-NP. Adanya peak baru mengindikasikan terbentuknya struktur baru jejaring ZnO dan WO3. ZnO-NP hasil sintesis memiliki ukuran kristalin sebesar 37.31 nm dan WO3-NP hasil sintesis memiliki ukuran kristalin sebesar 25.35 nm. Aktivitas fotokatalitik nanopartikel ZnO, WO3, dan nanomaterial ZnO-WO3 dilakukan pemodelan degradasi terhadap metilen biru. Aktivitas fotodegradasi metilen biru terjadi peningkatan dibawah sinar tampak dengan nanomaterial ZnO-WO3. Hasil menunjukan bahwa selama 90 menit, degradasi metilen biru menggunakan nanomaterial ZnO-WO3 sebesar 84.19 , sedangkan degradasi metilen biru menggunakan ZnO-NP sebesar 37.86 dan degradasi metilen biru menggunakan WO3-NP sebesar 40.65.

---

In this research, we synthesize ZnO NP, WO3 NP, and nanomaterial ZnO WO3 using tobacco leaves extract as a weak base source and capping agent. The synthesized nanoparticle and nanomaterial are characterized using FTIR, UV Vis DRS, and XRD. FTIR characterization shows that there are Zn O and W O bond for nanomaterial ZnO WO3. UV Vis DRS characterization shows that ZnO NP has a band gap of 3.21 eV, WO3 NP has a band gap of 2.30 eV, and nanomaterial ZnO WO3 has a band gap of 2.60 eV. XRD characterization shows that ZnO NP has a hexagonal crystal structure, WO3 NP has a triclinic crystal structure, and nanomaterial ZnO WO3 has some peaks combination of ZnO NP and WO3 NP, also there are some new peaks indicates there is a new structure which is ZnO NP and WO3 NP make a network. ZnO NP has a crystalline size of 37.31 nm and WO3 NP has a crystalline size of 25.35 nm. Photocatalytic activity of nanoparticles and nanomaterial is observed by degrading methylene blue as a model in this research. It shows an enhancement of fotodegradation activity of methylene blue under visible light using nanomaterial ZnO WO3 if it is compared with the ZnO NP and WO3 NP, which is under irradiation through 90 minutes, we obtain degradation of ZnO WO3 is 84.19 , whereas for ZnO NP is 37.86 and for WO3 NP is 40.65.