Karakteristik produk perlakuan permukaan thermo reactive deposition baja JIS-SUJ2 dengan serbuk pelapis Fe-Cr pada variasi temperatur proses = Product characteristics of thermo reactive deposition JIS-SUJ2 steel treatment with Fe-Cr coatings powder on process temperature variations

Muhammad Panji Wiguna; Myrna Ariati Mochtar, supervisor; Fandy Irwanto, supervisor; Nofrijon Sofyan, examiner; Wahyuaji Narottama Putra, examiner ([Publisher not identified] , 2018)

 Abstrak

ABSTRAK
Dalam penelitian ini telah dilakukan pengaruh variasi temperatur proses thermo-reactive deposition TRD terhadap pembentukan lapisan karbida pada substrat baja SUJ2 dengan metodepack cementation menggunakan serbuk Ferrochromium sebagai carbide former. Pada penelitian ini, dilakukan pencampuran antara serbuk carbide former dengan NH4Cl dan Al2O3 untuk diproses selama 6 jam di dalam furnace. Terdapat 3 variasi temperatur yaitu 900oC, 980oC, dan 1060o yang bertujuan untuk mengetahui pengaruh temperatur terhadap ketebalan, kehomogenan, kekerasan dan laju keausan lapisan karbida yang terbentuk. Setelah proses TRD dilakukan, pin baja SUJ2 dikarakterisasi. Ketebalan lapisan karbida yang terbentuk akan semakin meningkat dengan semakin tinggi temperatur dimana ketebalan pada temperatur 900oC, 980oC, dan 1060oC berturut-turut adalah 11,35 m, 19,89 m, dan 25,86 m. Ketebalan yang didapat cenderung homogen. Temperatur proses TRD tidak berpengaruh signifikan terhadap kekerasan lapisan karbida dengan kekerasan pada temperatur 900oC, 980oC, dan 1060oC adalah 1746,8 HV, 1751,6 HV dan 1753,4 HV. Laju keausan yang didapat pada temperatur 900oC, 980oC, dan 1060oC dengan metode Ogoshi adalah 7,25 x 10-4 mm3/m, 7 x 10-4 mm3/m dan 6,875 x 10-4 mm3/m. Hasil lapisan yang dikarakterisasi menggunakan difraksi sinar-X XRD menunjukkan bahwa lapisan terdiri dari karbida krom Cr23C6, Cr7C3, Cr3C2 . Pengamatan mikroskop optik memperlihatkan fasa substrat yang terdiri dari perlit dan sementit serta butir yang cenderung membesar dengan peningkatan temperatur.

ABSTRACT
In this study, the effect of thermo reactive deposition TRD temperature variation on the formation of carbide layer on SUJ2 steel substrate by pack cementation method using Ferrochromium powder as carbide former. In this study, mixing FeCr powders with NH4Cl and Al2O3 to process in furnace during 6 hours. There are 3 variation of temperatures 900 C, 980 C dan 1060 C. The effects of temperature on layer thickness, homogenity, hardness, and wear rate of the formed carbide layer. After process TRD is done, the SUJ2 steel pin is characterized. The thickness of the carbide layer formed will increase with higher temperatures where the thickness at temperatures of 900oC, 980oC, and 1060oC is 11,35 m, 19,89 m, and 25,86 m. The gained thickness tends to be homogeneous. TRD process temperature has no significant effect on hardness of the carbide layer with hardness at temperatures of 900oC, 980oC, and 1060oC is 1746,8 HV, 1751,6 HV and 1753,4 HV. The wear rate at temperatures of 900oC, 980oC, and 1060oC with the Ogoshi method was 7.25 x 10 4 mm3 m, 7 x 10 4 mm3 m and 6.875 x 10 4 mm3 m. The result layers characterized using X ray diffraction XRD showed that the coating consisted of chromium carbide Cr23C6, Cr7C3, Cr3C2 . Optical microscope observations show substrate phases consisting of pearlite and cementite and grains that tend to enlarge with increasing temperatures.

 File Digital: 1

Shelf
 S-Pdf-Muhammad Panji Wiguna.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2018
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xii, 70 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-Pdf 14-20-298696980 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20473551
Cover