Sintesis karbon mesopori terimpregnasi nanopartikel Ni sebagai katalis reaksi hidrogenasi karbon dioksida = Synthesis of mesoporous carbon-supported Ni nanoparticles for mesoporous carbon hydrogenation catalyst

Afif Zulfikar Pamungkas; Yuni Krisyuningsih, supervisor; Iman Abdullah, supervisor; Agustino Zulys, examiner; Aminah, examiner; Yoki Yulizar, examiner; Widayanti Wibowo, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018)

 Abstrak

ABSTRAK
Karbon mesopori telah berhasil disintesis dengan metode soft template menggunakan phloroglucinol dan formaldehida sebagai sumber karbon dan Pluronic F127 sebagai template. Material kemudian diimpregnasi dengan Ni II dilanjutkan dengan reduksi dengan H2 sehingga terbentuk nanopartikel Ni yang terimpregnasi dalam karbon mesopori. Analisis dengan XRD menunjukkan difraksi pada 25 dan 44o yang merupakan difraksi dari karbon grafitik. Selain itu difraksi pada 45 dan 52o menunjukkan keberadaan Ni 0 . Analisis EDX mengungkap kandungan Ni dalam beberapa karbon mesopori sebesar 0,1 hingga 24 . Analisis luas permukaan memberi informasi karbon mesopori memiliki luas permukaan sebesar 387,7 m2/g dan pori 7,4 nm. Impregnasi dengan Ni akan memperkecil luas permukaan maupun ukuran pori. Analisis dengan XPS mengonfimasi keberadaan Ni dengan bilangan oksidasi nol. Material digunakan sebagai katalis untuk reaksi hidrogenasi CO2. Reaksi hanya dapat berlangsung jika terdapat Ni 0 sebagai pusat aktif pada karbon mesopori. Semakin banyak Ni 0 semakin besar konversinya meskipun tidak berpengaruh terhadap persen hasil yield . Konversi terbesar didapat dari katalis Ni-MC 30 dengan konversi dan yield berturut-turut 94,6 dan 3,5 pada suhu 673 K.

ABSTRACT
Mesoporous Carbon has been successfully synthesized via soft template method using phlroglucinol and formaldehyde as carbon precursors and Pluronic F127 as template. The material was impregnated with Ni II and reduced with H2 to obtainNi metal. XRD analysis showed diffraction peaks on 25 and 44o which are characteristic of graphitic carbon. In addition, diffraction on 45 and 52o showed the existence of Ni 0 . EDX analysis showed the Ni content in mesoporous carbon, that was 0.1 to 24 . Surface area analysis gave information about surface area of 387.7 m2 g and pore diameter of 7.4 nm. Ni impregnation is presumed to reduce both surface area and pore diameter of mesoporous carbon. XPS analysis confirmed zero oxidation state of Ni. This material was used as catalyst for CO2 hydrogenation reaction. This reaction gave product only in the presence of Ni. The higher the Ni content the higher the conversion though the yield is unchanged. The highest conversion is shown by Ni MC 30 with conversion of 94.6 and yield of 3.5 at 673 K.

 File Digital: 1

Shelf
 T49910-Afif Zulfikar Pamungkas .pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T49910
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : x, 34 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T49910 15-21-819412308 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20477408
Cover