Modifikasi elektroda boron doped diamond dengan nanpartikel emas melalui green synthesis menggunakan ekstrak bawang putih (Allium Sativum) untuk sensor arsen = Modification of doped diamond boron electrode with gold nanoparticles through green systhesis using garlic extract (Allium Sativum) for arsenic sensors

Toto Raharto; Ivandini Tribidasari Anggraningrum, supervisor; Yoki Yulizar, supervisor; Jarnuzi Gunlazuardi, examiner; Widayanti, examiner; Iman Abdullah, examiner; Munawar Khalil, examiner (Fakultas Ilmu Pengetahuan Budaya Universitas Indonesia, 2018)

 Abstrak

ABSTRAK
Modifikasi boron-doped diamond (BDD) dengan emas nanopartikel (AuNPs) telah dikembangkan untuk sensor elektrokimia (yaitu deteksi arsenik). Nanopartikel emas (AuNPs) disintesis dengan ekstrak bawang putih bertindak baik sebagai reduktor dan zat penstabil. Dengan kondisi optimum 1.602 mmol Au dari HAuCl4 dalam perbandingan dengan 1 gr ekstrak bawang putih pada pH=5 di bawah radiasi UV. Karakterisasi dari AuNPs menggunakan peralatan UV-Vis Spectrofotometer yang dikonfirmasi pada panjang gelombang 520 nm, dan Transmission Electron Microscope (TEM)  didapati ukuran partikel sebesar 3.420 +/- 1.740 nm.  AuNPs yang telah disintesis dimodifikasi pada permukaan BDD dengan teknik perendaman di bawah iradiasi UV pada panjang gelombang 254 nm. SEM EDX menunjukkan bahwa BDD dimodifikasi AuNPs dengan rasio Au: C = 36.59 : 62.53 (wt%)  dapat berhasil disiapkan.  Aplikasi BDD yang sudah dimodifikasi dengan nanopartikel emas juga sukses digunakan untuk mengukur kadar arsen secara random pada danau UI, dengan hasil negatip, tidak ada kandungan Arsen (As3+)  pada danau UI.  

 

Kata kunci   : Nanopartikel,  Emas, Green Synthesis, Ekstrak, Bawang putih, Boron Doped Diamond, Sensor, Arsen.


Modifications of boron-doped diamond (BDD) with gold nanoparticles (AuNPs) have been developed for electrochemical sensors (i.e. arsenic detection). Gold nanoparticles (AuNPs) synthesized with garlic extract act as both reducing agents and stabilizers. Under optimum conditions 1,602 mmol Au from HAuCl4 in comparison with 1 gr of garlic extract at pH = 5 under UV radiation. The characterization of AuNPs using a UV-Vis spectrophotometer was confirmed at a wavelength of 520 nm, and the Transmission Electron Microscope (TEM) found particle size of 3,420 +/- 1,740 nm. The synthesized AuNPs were modified on the BDD surface by immersion techniques under UV irradiation at 254 nm wavelength. SEM EDX showed that AuNPs were modified by BDD with Au: C = 36.59: 62.53 (wt%) ratio can be successfully prepared. The BDD application that has been modified with gold nanoparticles was also successfully used to measure arsenic levels randomly on UI lakes, with negative results, no Arsenic content (As3+) on UI lakes.

Keywords  :  Nanoparticles, Gold, Green Synthesis, Extracts, Garlic, Boron Doped Diamond, Sensors, Arsenic

 File Digital: 1

Shelf
 T52389-Toto Raharto.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T52389
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Ilmu Pengetahuan Budaya Universitas Indonesia, 2018
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvii, 75 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T52389 15-21-332798441 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20486371
Cover