Sintesis komposit Li4Ti5O12/SiC dengan reaksi solid-state sebagai material Anoda Baterai Ion Litium = Li4Ti5O12/SiC composite synthesis through solid-state reaction as anode material for lithium ion battery

Said Firdaus; Bambang Priyono, supervisor; Anne Zulfia, examiner; Achmad Subhan, examiner (Fakultas Teknik Universitas Indonesia, 2019)

 Abstrak

Litium Titanat (LTO) merupakan salah satu material anoda dengan performa yang baik karena sifatnya yang zero - strain. Pada penelitian ini sintesis LTO dilakukan dengan menggunakan metode solid-state dimana menggunakan serbuk LiOH dan TiO2 sebagai prekursor. Akan tetapi, LTO memiliki kapasitas yang cukup rendah. Penambahan Silikon Karbida (SiC) dilakukan untuk meningkatkan kapasitas dan stabilitas kapasitas pelepasan pada LTO. Penambahan SiC dilakukan setelah proses sintesis LTO selesai menggunakan metode wet ball mill.
Hasil sintesis menghasilkan serbu berwarna keabuan. Serbuk LTO/SiC dikarakterisasi menggunakan difraksi sinar-X (XRD), SEM-EDS dan EIS. Hasil XRD menunjukkan LTO/SiC telah berhasil terbentuk sebagai produk utama. Selain itu, hasil pengujian performa EIS menunjukkan bahwa LTO/SiC 4% memiliki konduktivitas tertinggi dimana ditunjukkan dengan resistivitasnya yang paling rendah dibanding yang lain. Selain pengujian tersebut, untuk menguji performa LTO/SiC dilakukan pengujian CV dan CD.

Lithium Titanate (LTO) is one of the anode materials which possess very good electrochemical performance because of its zero-strain characteristic. In this study, Solid-state synthesis method was used to synthesize LTO using LiOH and TiO2 powder as precursors. However, LTO performance is limited by its low capacity. Addition of Silicon Carbide (SiC) was done using wet ball mill method to enhance its capacity and stability of discharge capacity.
As a result, the powder has greyish color. LTO/SiC powder was characterized using X-Ray Diffraction (XRD), SEM-EDS and EIS. The result of XRD characterization exhibits the formation of LTO/SiC as a major products. Moreover, EIS performance testing showed that LTO/SiC 4% possess highes electrical conductivity which is indicated by its lowest resistivity compared to other sample. Furthermore, to find out performaces of LTO/SiC, CV and CV test was performed.

 File Digital: 1

Shelf
 S-Said Firdaus.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Skripsi Membership
No. Panggil : S-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2019
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xiii, 47 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
S-Pdf 14-20-891517776 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20490001
Cover