Karakteristik zirconium silicate sebagai foundry coating dengan penambahan alumina dan talek sebagai filler refractory = Characteristic of zirconium silicate as foundry coating wirh the addition of alumina and talc as refractory filler

Agy Randhiko; Donanta Dhaneswara, supervisor; Nofrijon Sofyan, examiner; Alfian Ferdiansyah Madsuha, examiner; Jaka Fajar Fatriansyah, examiner (Fakultas Teknik Universitas Indonesia, 2020)

 Abstrak

Alumium merupakan material yang dominan digunakan dalam dunia industri, industri manufaktur banyak menghasilkan produk aluminium dengan metode casting. Salah satu yang perlu diperhatikan dalam proses pengecoran adalah coating. Coating pada proses pengecoran bertujuan mengurangi kejutan termal. Zirkon merupakan material yang biasa dipakai sebagai material pengisi, tetapi zirkon memilik harga yang relative mahal, sehingga pada penelitian ini akan dibahas pengaruh dari material pengisi alumina dan talc terhadap zirkon untuk menghasilkan refractory coating yang baik. Penelitian ini berfokus pada variasi konsentrasi dan juga temperatur pengeringan yang ideal sehingga didapatkan coating yang baik. Analisa pada penelitian ini antara lain Pengujian X-Ray Diffraction (XRD), X-Ray Flourensi (XRF), Particle Size Analyzer (PSA), viscosity, thermal analysis mengguanakan differential thermal analysis (DTA), pengambilan gambar dilakukan dengan Scanning Electron Microscope (SEM) yang dilengkapi oleh fasilitas EDX untuk mengetahui kandungan material yang ada pada material coating. Pengujian pull off strength dilakukan untuk mengetahui sifat adhesive dari material coating. Konduktivitas termal dilakukan untuk mengetahui nilai konduktivitas termal dari lapisan coating. Hasil dari pengujian bahwa material alumina dan talc dapat digunakan sebagai filler material bahan baku refractory coating. Ukuran partikel kecil dapat mempercepat proses homogenisasinya, sementara distribusi partikel berpengaruh terhadap konsentrasi tegangan. Bahan baku ball mill lebih baik distibusi partikelnya.

Alumium is the dominant material used in the industrial company, many manufacturing industries produce aluminum products by the casting method. Coating is one that needs to be considered in the casting process. Coating in the casting process helps reduce thermal shock. Zircon is a material commonly used as a filler, but the zircon has a relatively expensive price, so this research will discuss alumina fillers and talc to zircon to produce a good fire resistant coating. This research focused on variation and ideal temperature so that a good coating was obtained. The analysis in this study include X-Ray Diffraction Testing (XRD), X-Ray Flourence (XRF), Particle Size Analyzer (PSA), viscosity, thermal analysis using differential thermal analysis (DTA), image capture is done by Scanning Electron Microscop (SEM) which is equipped by EDX facilities to find out the content in the material coating. Pull off strength testing is carried out to study the adhesive properties of the coating material. Thermal conductivity is carried out to determine the thermal conductivity value of the coating. Alumina materials and talc can be used as fillers for refractory coatings. Small particle size can accelerate the process of homogenization, while particle distribution affects the stress concentration. The ball mill raw material is better to distribute the particles.

 File Digital: 1

Shelf
 T55226-Agy Randhiko.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T55226
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2020
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvi, 81 pages : illustrations ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T55226 15-21-932693895 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20499363
Cover