Studi pengaruh variasi penambahan serbuk alumunium paduan (A356.2) pada cat epoksi terhadap daya lekat dan ketahanan korosi pelat baja karbon ASTM A36 di lingkungan laut = Study of effect variation addition of aluminum alloy powder (A356.2) in epoxy paint on the adhesion and corrosion resistance of ASTM A36 carbon steel plates in marine environment

Andri Hermawan; Rini Riastuti, supervisor; Rizal Tresna Ramdhani, supervisor; Sutopo, examiner; Johny Wahyuadi Mudaryoto, examiner; Yunita Sadeli, examiner (Fakultas Teknik Universitas Indonesia, 2019)

 Abstrak

Salah satu permasalahan penggunaan baja karbon pada anjungan lepas pantai adalah korosi, yang dapat menyebabkan penipisan dan kerusakan pada struktur baja. Oleh karena itu diperlukan perlindungan untuk material baja tersebut agar terjaga dari korosi eksternal sampai waktu yang telah ditentukan. Penelitian ini bertujuan untuk mempelajari mekanisme perlindungan korosi dan mekanisme kelekatan cat epoksi yang ditambahkan serbuk aluminium paduan A356.2, yang diaplikasikan pada material pelat baja karbon ASTM A36 di dalam larutan klorida. Metode pengujian meliputi uji tarik cat, uji gores dan sembur garam, pengamatan makro, pengamatan mikro, SEM dan EDX, uji EIS dan Polarisasi. Hasil penelitian menunjukan sistem pengecatan yang menggunakan campuran epoksi 100 ml yang ditambahkan 50 gram serbuk A356.2 memiliki ketahanan korosi yang tinggi dan campuran serbuk A356.2 dapat berfungsi sebagai material penghalang dari korosi eksternal di lingkungan laut.

One of the problems with the utilization of carbon steel in offshore platforms is corrosion, which can cause thinning and damage to steel structures. Therefore, steel material needs to be protected from external corrosion until a predetermined time. This study aims to investigate the mechanism of corrosion protection and the sticking mechanism of epoxy paint with A356.2 aluminum alloy powder, which was applied to ASTM A36 carbon steel plate material in chloride solution. The test methods include paint tensile test, scratch and salt spray test, micro observation, macro observation, SEM, EDX, EIS test, and Polarization. The results of the research show that painting system containing 100 ml epoxy mixture with addition of 50 grams of A356.2 powder has high corrosion resistance and the powder mixture A356.2 can function as a barrier from external corrosion in marine environment.

 File Digital: 1

Shelf
 T-Andri Hermawan.pdf :: Unduh

LOGIN required

 Metadata

Jenis Koleksi : UI - Tesis Membership
No. Panggil : T-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Program Studi :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2019
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xv, 108 pages : illustration + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
  • Sampul
No. Panggil No. Barkod Ketersediaan
T-pdf 15-22-84309223 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20499728
Cover